Reinforcement Bar PDF_new - Raajratna

Product PropertiesReinforcement BarsChemical CompositionPRODUCTION PROCESSCOLD DRAWN/HOT ROLLEDC MnGRADE Max Max% %1.4301-304 0.080 2.001.4401-316 0.080 2.001.4571-316Ti 0.080 2.001.4362 [Duplex] 0.030 2.001.4462 [Duplex] 0.030 2.00PMax%0.0450.0450.0450.0300.030SMax Max Max Min% % % % % % % %0.0300.0300.0300.0200.020Si Cr Ni Cu Mo N Ti1.001.001.001.001.0018.00-20.00 8.00-10.00 - - - - - -16.00-18.00 10.00-14.00 - - - 2.00-3.0016.00-18.00 10.00-14.00 - - - 2.00-3.0022.00-24.00 3.50-5.50 0.10-0.60 0.10-0.6021.00-23.00 4.50-6.50 0.10-0.60 2.50-3.500.11 - - -0.11 - - -0.11 5xC0.05-0.20 - - -0.10-0.22 - - -Mechanical PropertiesPRODUCTION PROCESSCOLD DRAWNGRADE1.4301-3041.4401-3161.4571-316Ti1.4362 [Duplex]1.4462 [Duplex]1.4301-3041.4401-3161.4571-316Ti1.4462 [Duplex]SizeinMM3 - 163 - 163 - 163 - 163 - 1616 - 2516 - 2516 - 2516 - 25TensileStrengthN/MM²600600600800800600600600700Yield % Elongation T. S. /Strength Aj A10 0.2 % YieldN/MM² 5505503315151.081.085503 151.056003 151.086003 151.085003 151.085003 151.085003 151.055003 151.08Mechanical PropertiesPRODUCTION PROCESSHOT ROLLED1.4301-3041.4401-3161.4571-316Ti1.4462 [Duplex]Size Tensile Yield % ElongationGRADE in Strength Strength Aj A10MM N/MM² N/MM² 16 - 50 600 500 3 151.0816 - 50 600 500 3 151.0816 - 50 600 500 3 151.0816 - 50 600 500 3 151.08A10T. S. /0.2 % YieldAjElongation :Aj = 100 mm marked before tension measured after tension to fracture measuring point 2.5 x diameter from fracture.A10 = Diameter x 10 marked before tension measured after tension to fracture measured across fracture.05