Polymer Emulsion And Cement Based, Double Component,<br />
Semi Elastic Waterproofing Material<br />
PRODUCT DESCRIPTION<br />
Semi elastic waterproofing material comprised of cement based powder component and<br />
polymer emulsion based liquid component, which can be applied prior to the top coating<br />
material.<br />
AREAS OF USE<br />
Megaİzo Lastik 7 is applied for waterproofing before the top coating material in such wet<br />
spaces as bathrooms, kitchens and balconies, in terraces, and in such wet spaces as<br />
decorative pools and small sized water tanks. It is suitable for use on horizontal and vertical<br />
surfaces of indoors and outdoors spaces.<br />
double coat on the surface. Once the primary coat thoroughly dries, the secondary coat<br />
should be applied as perpendicularly to the primary coat.<br />
• Edge and corner joints should be beveled with MegaTamir İ and MegaTamir K repair<br />
mortars in order for the maintenance of waterproofing.<br />
• In the cases, where beveling is not performed; Megaİzo Bant should be applied to such<br />
inadequately waterproof spots as edge and corner joint spots in order to ensure the<br />
maintenance of insulation.<br />
• Depending on the nature of the application surface; the secondary coat may be applied after<br />
the placement of Megaİzo File on the primary coat. In the cases, where net reinforcement is<br />
necessary; the net shall be laid on the primary coat before it dries.<br />
56<br />
PRODUCT ADVANTAGES<br />
• Highly adhesive.<br />
• Being of water repellant nature, the product is resistant to water and frost.<br />
• Ensures seamless waterproofing for application surfaces.<br />
• Allows for the application of any coating material subsequent to the application thereof.<br />
• Semi elastic.<br />
• Applied rapidly and easily.<br />
• Not contain solvents, and is environmentally friendly.<br />
PERFORMANCE<br />
TYPE: CM P, waterproofing material with cement content, applied in liquid form, chlorinated<br />
water resistant, poses crack bridging capability.<br />
Initial adhesion strength ≥ 0.5 N/mm 2 TS EN 14891 : 2012<br />
Adhesion strength after water contact ≥ 0.5 N/mm 2 TS EN 14891 : 2012<br />
Adhesion strength after thermal ageing ≥ 0.5 N/mm 2 TS EN 14891 : 2012<br />
Adhesion strength after freezing - thawing<br />
cycles<br />
≥ 0.5 N/mm 2 TS EN 14891 : 2012<br />
Adhesion strength after hard water contact ≥ 0.5 N/mm 2 TS EN 14891 : 2012<br />
Waterprooding<br />
No penetration, ≤<br />
20 gr increase in TS EN 14891 : 2012<br />
mass<br />
Crack bridging capability under standard<br />
conditions<br />
≥ 0.75 mm TS EN 14891 : 2012<br />
Adhesion strength after chlorinated water ≥ 0.5 N/mm 2 TS EN 14891 : 2012<br />
The foregoing values represent the results of the laboratory tests conducted at 23 ± 2°C<br />
temperature and 50% ± 5 relative humidity conditions. The values provided as per the table<br />
may vary depending on the surface and ambient conditions.<br />
REFERENCE STANDARDS<br />
Certifications/Standards<br />
TS EN 14891<br />
TS EN 1504 - 2<br />
Ministry of Public Works and Settlement Item No.<br />
Ministry of Public Works and Settlement Item No.: 04.477/2<br />
QUALITY CERTIFICATES<br />
TSE<br />
CE<br />
APPLICATION PROCEDURE<br />
Application Surfaces<br />
Indoors and Outdoors Walls;<br />
- Cement based plaster (MegaFilm primer applied)<br />
- Concrete (MegaFilm or MegaFilm BB primer applied)<br />
Indoors and Outdoors Floors;<br />
- Cement based trowel coating (MegaFilm primer applied)<br />
- Concrete (MegaFilm or MegaFilm BB primer applied)<br />
Surface Preparation<br />
• Application surfaces should be sound, clean, dust-free, and free from molding oils and<br />
other foreign substances. Such materials as mortar and cement residues should be peeled off.<br />
• The surface defects, which are deeper than 1 cm, should be repaired with MegaTamir İ or<br />
MegaTamir K 24 hours in advance. In the cases, where structural repair mortar should be<br />
used; MegaTamir İ Yapısal or MegaTamir K Yapısal should be preferred.<br />
• Upon the completion of the surface cleaning, MegaFilm primer should be applied in a<br />
single coat with a brush and be left to dry for 1 to 2 hours in order to enhance the bonding<br />
strength and stabilize the surface absorption.<br />
• Exposed concrete surfaces should be applied MegaFilm BB exposed concrete primer in<br />
single coat and be left to dry for minimum 3 hours prior to the application of the adhesive<br />
mortar in order to enhance the adhesion strength.<br />
Application Methods<br />
• Megaİzo Lastik 7, the mixture of which should have been prepared, should be applied in<br />
Application Recommendations<br />
• Due care must be taken to ensure that the insulation material is not damaged by mechanical<br />
impacts in the cases of coating over the insulation.<br />
• The product should not be applied against negative water pressure.<br />
• The product should, once mixed, be used before the expiration of its pot life. Any product,<br />
the pot life of which has expired, should not be used during the application.<br />
• Any foreign material should not be added into the product’s components of the product<br />
during the application.<br />
• The product should not be applied on unsound surfaces. The soundness and the load<br />
bearing capacity of old surfaces should be checked prior to adhesion.<br />
• The surface should be preserved from air currents and water contact during and after the<br />
application.<br />
• The product should not be applied to such surfaces, which are exposed to risk of freezing<br />
within the next 24 hours, which are frozen or the frost of which is thawing.<br />
• Due care should be given to prevent the exposure of the material to direct sunlight in hot<br />
weather conditions.<br />
• The product should not be applied on extremely windy weather conditions or on hot surfaces,<br />
which are exposed to direct sunlight; and in the cases, where application is imperative under<br />
such conditions, the environment and the surface should be prepared for application in<br />
advance.<br />
• The product should not be applied in rainy weather conditions, and the application surface<br />
should be preserved from rain for a period of 24 hours.<br />
• Refer to our technical support hotline for recommendation on different surface applications.<br />
(PHONE: 444 4 595)<br />
Surface and Ambient Temperature<br />
The surface and ambient temperature should be between +5°C and +35°C whilst at<br />
application.<br />
Application Limits<br />
Useful time for prepared mixture - Pot life<br />
Stand by period between coats<br />
Required standby time before subsequent application<br />
The foregoing values represent the results of the laboratory tests conducted at 23 ± 2°C<br />
temperature and 50% ± 5 relative humidity conditions. The values provided as per the table<br />
may vary depending on the surface and ambient conditions.<br />
APPLICATION INSTRUCTIONS<br />
Mixing Ratio<br />
The powder component (20 kg) and the liquid component (6 kg) should be thoroughly<br />
mixed.<br />
Mixing Equipment<br />
• Low speed electrical mixer (400 cycles/min.)<br />
• Special tip stirring equipment<br />
Mixing Period<br />
The product should be stirred with a low-speed mixer until any dry dust and globs are<br />
eliminated. The mortar should, then, be stirred once again for 1 to 2 minutes after being had<br />
settled for 3 to 4 minutes following preparation.<br />
Application Equipment<br />
• Brush<br />
• Roller<br />
Maximum 3 hours<br />
Minimum 6 hours<br />
Minimum 3 days<br />
Equipment Cleaning<br />
The equipment used should be cleaned with water following the application before the<br />
product dries.<br />
TECHNICAL PROPERTIES<br />
Chemical Structure: Cement and polymer emulsion based waterproofing material<br />
Dry Density: 0.98 ± 0.01 gr/cm 3