Platinalegeringen<br />
legering smeltinterval<br />
in ° Celsius<br />
Pt/Cu 960/=<br />
Pt/Co 950/=<br />
Pt/Pd 900/30<br />
Pt/Ir 800/200<br />
Pt/W 950/=<br />
Pt 999.5<br />
1730 - 1745<br />
1730 - 1740<br />
1540 - 1610<br />
1815 - 1830<br />
1840 - 1860<br />
1769<br />
Palladiumlegeringen<br />
legering smeltinterval<br />
in ° Celsius<br />
Pd 950/=<br />
Pd 999.5<br />
1380 - 1450<br />
1554<br />
Legeringsgids<br />
S.M.(g/cm 3<br />
) hardheid in<br />
gegloeide<br />
20,3<br />
20,5<br />
18,3<br />
21,7<br />
21,0<br />
21,4<br />
staat (HV)<br />
110<br />
130<br />
210<br />
190<br />
150<br />
40<br />
S.M.(g/cm3)<br />
hardheid in<br />
gegloeide<br />
11,8<br />
12,0<br />
staat (HV)<br />
hardheid<br />
60% koud<br />
Soldeeroverzicht platina en palladiumlegeringen<br />
groep gehalte legering-<br />
nummer<br />
platina<br />
palladium<br />
-<br />
-<br />
PT1<br />
PT3<br />
Pd1<br />
Pd2<br />
Pd3<br />
smelt-<br />
temperatuur<br />
95<br />
50<br />
in ° Celsius<br />
1400 – hard<br />
1090 – zacht<br />
1110 – hard<br />
980 – middel<br />
730 – zacht<br />
hardheid<br />
60% koud<br />
vervormd (HV)<br />
vervormd (HV)<br />
aanbevolen<br />
vloeimiddel<br />
geen<br />
geen<br />
165<br />
120<br />
vloeimiddel B<br />
vloeimiddel B<br />
vloeimiddel B<br />
Waarvoor welke <strong>Schöne</strong> platinalegering gebruiken<br />
legeringstype eenvoudige<br />
bewerking<br />
vlakke<br />
sieraden<br />
platina<br />
Pt/Cu 960/=<br />
Pt/Co 950/=<br />
Pt/Ir 800/200<br />
palladium<br />
Pd 950/=<br />
*<br />
*<br />
*<br />
gieten emailleren persen/<br />
forceren<br />
*<br />
*<br />
*<br />
*<br />
*<br />
185<br />
225<br />
295<br />
260<br />
220<br />
80