Hetron™ epoxy vinyl ester resins - CRECO, Inc.
Hetron™ epoxy vinyl ester resins - CRECO, Inc.
Hetron™ epoxy vinyl ester resins - CRECO, Inc.
Create successful ePaper yourself
Turn your PDF publications into a flip-book with our unique Google optimized e-Paper software.
Chemical Environment<br />
Notes<br />
Concentration<br />
Temperature (°C and °F) for<br />
HETRON Resin<br />
922 980 980/35 FR 992 FR 998/35 800 197<br />
(%) °C / °F °C / °F °C / °F °C / °F °C / °F °C / °F °C / °F<br />
Zinc Sulfate - 100 100/210 100/210 100/210 100/210 - 120/250 120/250<br />
Zinc Sulfite - 100 80/180 80/180 80/180 80/180 80/180 - -<br />
Zinc, Metal plating (See Metal<br />
plating)<br />
Notes<br />
Concentration chart<br />
ppm = %<br />
10,000 1 .0<br />
1,000 0 .1<br />
100 0 .01<br />
See pages 50 and 51 for notes<br />
- - - - - - - - -<br />
Baumé<br />
(°B,°Be or °Bé)<br />
Hydrochloric<br />
acid %<br />
Baumé concentration chart at 25°C, 77°F<br />
Nitric acid % Phosphoric<br />
acid %<br />
5 7 .15 7 .01 5 .28<br />
Sulfuric acid % Ammonia<br />
10 14 .83 12 .86 13 .70 10 .77 0 .<br />
16 24 .57 20 .69 21 .30 17 .53 10 .28<br />
19 29 .65 24 .83 25 .80 21 .07 15 .28<br />
22 35 .21 29 .07 30 .00 24 .61 21 .60<br />
24 39 .41 31 .94 34 .00 27 .10 25 .50<br />
30 41 .30 40 .20 34 .60<br />
35 50 .32 49 .50 41 .30<br />
40 61 .38 55 .00 48 .10<br />
46 81 .10 64 .60 56 .50<br />
48 91 .35 66 .00 59 .20<br />
62 90 .00 81 .30<br />
62 .5 96 .00 90 .60<br />
66 94<br />
____________________________________________________________________________<br />
____________________________________________________________________________<br />
____________________________________________________________________________<br />
____________________________________________________________________________<br />
____________________________________________________________________________<br />
____________________________________________________________________________<br />
____________________________________________________________________________<br />
____________________________________________________________________________<br />
____________________________________________________________________________<br />
____________________________________________________________________________<br />
____________________________________________________________________________<br />
79