Crack growth rate[mm/cycle] 10 -5 10 -6 10 -7 10 -8 10 -1 10 -9 Comparison A1N-A4T 26 = 240 MPa 10 0 Crack length [mm] o A1N • A4T 10 1 Crack growth rate[mm/cycle] Dipartimento di meccanica 10 -5 10 -6 10 -7 10 -8 10 -1 10 -9 = 180 MPa 10 0 Crack length [mm] o A1N • A4T 10 1
Interrupted test and crack propagation test 240 MPa W54(2.5E6) – W52_interrupted(2E6) (240 MPa) W52 W54 Dipartimento di meccanica
Page 1 and 2: Wolaxim final meeting 24 th -25 th
Page 3 and 4: Wolaxim experimental plan and aims
Page 5 and 6: Materials 5 30CrMb Bainitic microst
Page 7 and 8: Summary of A1N tests • End life t
Page 9 and 10: Summary of A4T tests • End life t
Page 11 and 12: Tests on 30CrMb material For 30CrMb
Page 13 and 14: Observations • Atmospheric corros
Page 15 and 16: Corrosion fatigue process 15 Dipart
Page 17 and 18: First stage of the Fatigue Life 180
Page 19 and 20: Damage of the surface 19 • Chemic
Page 21 and 22: Probability 0.99 0.96 0.90 0.75 0.5
Page 23 and 24: Probability 0.99 0.96 0.90 0.75 0.5
Page 25: Crack propagation tests Microdrille
Page 29 and 30: Crack growth rate A4T 320 MPa Confr
Page 31 and 32: Propagation of single cracks A4T 40
Page 33 and 34: Interrupted test and crack propagat
Page 35 and 36: Prove Full-Scale
Page 37 and 38: Full scale test A4T = 360 MPa Stop
Page 39 and 40: Plastic replica 1e6 cicli 0° Dipar
Page 41 and 42: Plastic replica 2.2e6 cicli 0° Dip
Page 43 and 44: Mechanical cleaning- 4.317e6 cycles
Page 45 and 46: Full scale test A4T = 240 MPa Stop
Page 47 and 48: Plastic replica 2e6 cycles Dipartim
Page 49 and 50: TWI Digital Microscope - 2e6 cycles
Page 51 and 52: TWI Digital Microscope - 2e6 cycles
Page 53 and 54: Assile 038 - Replica 6e6 cicli Dipa
Page 55: Conclusion • Agreement between cr