SPRING STEEL
FASTENERS
Standard Finishes For Tinnerman ® Fasteners.
Listed below are the most commonly used finishes available for protective coating and rust-proofing Tinnerman
Brand Fasteners. To specify desired finish use corresponding dash number, shown below as the last dash number,
affixed to the Part Number. Examples: C 183-012-27, C 1053-012-4, C 1158-5610-1 FINISH
PURCHASE PARTNERS
2369 Schuetz Road
Saint Louis, Missouri 63146
Phone: 314-567-8585
Fax: 314-567-7334
Email: sales@purchasepartners.com
Tinnerman® is the registered trademark of
Tinnerman Palnut Engineered Products LLC
-27
(Soluble Oil
Dipped)
-4
(Phosphate and
Oil)
-1
(Phosphate and 2
Coats Olive Drab
Paint)
-67
(Phosphate and 2
Coats Aluminum
Paint)
-373
(Phosphate, 2
Coats of Paint and
Oil)
Natural.
Black.
Olive drab
Aluminum color
smooth appearance.
Bright green.
SALT SPRAY TEST
5% solution at 95°F. Fer­rous parts: first
rust spots after 1 hour, end point (1116" dia.
rust spots) after 21/2 hours. Non-ferrous
parts: corrosion will be normal for the plain
fin­ish of the material.
5% solution at 95°F. First rust spots after
32 hours. End point (V16" dia. rust spots)
after 40 hours
5% solution at 95°F. First rust spots after
48 hours. End point (1/16" dia. rust spots)
after 100 hours
5% solution at 95°F. First rust spots after
48 hours. End point (1/16" dia. rust spots)
after 100 hours.
5% solution at 95°F. First rust spots after
150 hours. End point (1/16" dia. rust spots)
after 250 hours.
NOTE: The following electroplate finishes are limited to only a few parts, such as Tubular Type Clips and
Tube Clamps. Please do not specify these finishes for other types of Tinnerman Fasteners without the
approval of our engineering department.
-600
(Zinc Mechanical
plate)
-38
(Zinc Electroplate)
-24
(Cadmium Electroplate)
Satin Silver Color
Silver color. Slight
discoloration from
baking may occur
Silver color. Slight
discoloration from
baking may occur.
5% solution at 95°F. End point (red rust)
after 24 hours.
5% solution at 95°F. End point (red rust)
after 36 hours.
5% solution at 95°F. First rust spont after
48 hours. End point (V16" dia. rust spots)
after 75 hours.