<strong>Dinitrol</strong> <strong>AV</strong> 8<br />
Corrosion Inhibiting Compound<br />
Characteristics:<br />
Range of use:<br />
Super penetrating water displacing, corrosion inhibiting compound, leaving tack - free,<br />
firm film.<br />
For protection of all, commonly used aerospace metals and alloys.<br />
DINITROL <strong>AV</strong> 8 can be used in all areas of the airframe. In areas exposed to severe<br />
corrosion conditions over-coating with the heavy duty compound DINITROL <strong>AV</strong> 100D<br />
is required.<br />
Movable parts should be masked before treatment, unless sufficient control of the<br />
spray is possible. If not possible, the use of the soft, waxy DINITROL <strong>AV</strong> 25 is<br />
recommended.<br />
Application:<br />
DINITROL <strong>AV</strong> 8 can be applied by dipping, brushing or spraying.<br />
It can be sprayed using the DINITROL ACS - SYSTEM (airmix),or the DINITROL<br />
AIRLESS APPLICATION SYSTEM.<br />
Applicable<br />
Specifications<br />
and Approvals: Meets or exceeds :-<br />
The operational data for the spraying equipment can be found in the DINITROL<br />
<strong>AV</strong>IATION TECHNICAL MANUAL.<br />
For personal safety precautions see the Material Safety Data Sheet.<br />
MIL-C-16173D<br />
and is approved by :-<br />
AIRBUS INDUSTRIE TN 007.10138, TYPE I, GRADE 3<br />
BOEING MATERIAL SPECIFICATION BMS 3-23 F, TYPE II<br />
BOMBARDIER CMS 565-06, TYPE I<br />
MCDONNELL DOUGL<strong>AS</strong> DMS 2150<br />
ATR<br />
FOKKER AIRCRAFT B.V.<br />
GULFSTREAM AEROSPACE<br />
PILATUS<br />
PIPER<br />
LOCKHEED MARTIN CORPORATION<br />
EMBRAER<br />
A company of mg chemical group Dynamit Nobel
Page 2/2<br />
PHYSICAL PROPERTIES<br />
<strong>Dinitrol</strong> <strong>AV</strong> 8<br />
Test Method Value & Unit<br />
Flash point SS 021811 47 o C<br />
Viscosity DIN Cup 2 71 sec.<br />
<strong>AS</strong>TM D 445<br />
16 cSt<br />
Non-volatile content <strong>AS</strong>TM D 1644 44% by weight<br />
Calculated<br />
35% by volume<br />
Type of solvent<br />
Aliphatic hydrocarbon with 0.5% aromatics max.<br />
Density SS 184111 880 kg/m 3<br />
Coverage Calculated >44 m 2 /l at 8µ<br />
Storage and application temperature 15 o C, min.<br />
Shelf life<br />
36 months from filling date<br />
FILM PROPERTIES<br />
Test Method Value & Unit<br />
Colour<br />
Transparent, slightly brown tinted<br />
Specific film weight Weighing 8 g/m 2<br />
Approximate film thickness 8µ<br />
Penetration SS 186017 >80 mm<br />
BMS 3-23<br />
Pass,100%<br />
Water displacement ability SS 186018 0% corrosion<br />
Drying time<br />
40 min tack - free<br />
Low temperature adhesion BMS 3-23 No flaking<br />
Low temperature flexibility BMS 3-26 No flaking<br />
Removable with solvent<br />
Yes<br />
Burning properties DEF-STAN 80-83/1 Self extinguishing<br />
Freedom from flow<br />
>4h at 100 o C<br />
RESISTANCE VALUES<br />
Test Method Value & Unit<br />
Salt spray test <strong>AS</strong>TM B 117<br />
on steel >300h (at mark 7)<br />
on 2024-T3 >1500h (at mark 7)<br />
Humidity <strong>AS</strong>TM D 1748 >2000h (at mark 7)<br />
Resistance against 5% NaOH 24h on cured film Not attacked<br />
10% CH 3 COOH 24h on cured film Not attacked<br />
5% HNO 3 24h on cured film Not attacked<br />
20% HCl 24h on cured film Not attacked<br />
Exfoliation <strong>AS</strong>TM G 34 Pass<br />
Compatibility with Cd BMS 3-23 Pass<br />
ph October 2001<br />
® Registered trademark<br />
The above data have been compiled to the best of our knowledge on the basis of<br />
thorough tests and with regard to the current state of our long practical experience. No<br />
liabilities or guarantee deriving from or in connection with this leaflet can be imputed to us.<br />
Reproduction, in whole or in part, only with our express permission.