AQUEOUS CORROSION RESISTANCE (continued)<br />
Effect of Cold Work Upon Corrosion Resistance in Boiling 20% HCl*<br />
Ultimate<br />
Corrosion<br />
Tensile Yield Strength Elongation Rate<br />
% Hardness Strength at 0.2% Offset in 2" (51mm) PerYear<br />
Coldwork Rc Ksi MPa Ksi MPa % EL Mils (mm)<br />
0 18 125 860 62 425 57 13 (0.33)<br />
10 30 140 965 100 690 40 13 (0.33)<br />
20 37 159 1095 130 895 25 13 (0.33)<br />
30 41 180 1240 154 1060 13 13 (0.33)<br />
40 44 202 1395 172 1185 9 13 (0.33)<br />
50 46 221 1525 183 1260 8 13 (0.33)<br />
* Exposure for four 24 hour periods<br />
HASTELLOY ® B-3 ® <strong>alloy</strong> ISOCORROSION DIAGRAMS<br />
Hydrochloric Acid<br />
Sulfuric Acid<br />
250<br />
Boiling Point Curve<br />
125<br />
400<br />
350<br />
>5 mpy<br />
(>0.13 mmpy)<br />
200<br />
200<br />
>5 mpy<br />
(>0.13 mmpy)<br />
100<br />
300<br />
250<br />
Boiling Point Curve<br />
150<br />
150<br />
100<br />
0<br />
5 to 20 mpy<br />
(0.13 to 0.51 mmpy)<br />
0 to 5 mpy<br />
(0.13 mmpy)<br />
10 20 30<br />
Concentration, wt.%<br />
40<br />
75<br />
50<br />
200<br />
150<br />
100<br />
0<br />
>5 mpy<br />
(>0.13 mmpy)<br />
10<br />
20<br />
30<br />
0 to 5 mpy<br />
(0 to 0.13 mmpy)<br />
40 50 60 70 80 90 100<br />
Concentration, wt.%<br />
100<br />
50<br />
350<br />
Phosphoric Acid<br />
300<br />
150<br />
250<br />
125<br />
200<br />
Boiling Point Curve<br />
>5 mpy<br />
(>0.13 mmpy)<br />
100<br />
150<br />
100<br />
0 to 5 mpy<br />
(0 to 0.13 mmpy)<br />
75<br />
50<br />
0<br />
10<br />
20<br />
30 40 50 60 70 80<br />
Concentration, wt.%<br />
HASTELLOY ® B-3 ® <strong>alloy</strong><br />
6