High Performance Solid Carbide Tools - Rapp Industrial Sales
High Performance Solid Carbide Tools - Rapp Industrial Sales
High Performance Solid Carbide Tools - Rapp Industrial Sales
You also want an ePaper? Increase the reach of your titles
YUMPU automatically turns print PDFs into web optimized ePapers that Google loves.
Ti-NAMITE®<br />
Tool Coatings<br />
are specifically<br />
engineered for SGS ®<br />
solid carbide rotary<br />
tools. This proprietary<br />
multi-layering<br />
process results in<br />
maximized tool life<br />
and increased speed<br />
and feed rates in<br />
any application.<br />
Hardness: 3300HV0.05<br />
Recommended For Your Applications In...<br />
• Cast Iron<br />
• <strong>High</strong>-temperature Alloys<br />
• Hardened Steels<br />
• Stainless Steels<br />
Ti-NAMITE-A (AlTiN) is Preferred for <strong>High</strong>-speed and<br />
Dry Cutting<br />
Oxidation Temperature:<br />
800°C - 1472°F<br />
Coefficient Of Friction:<br />
.45<br />
Thickness: 1 - 4 Microns<br />
(based on tool diameter)<br />
Drilling Hardened Tool Steel<br />
Tool Type<br />
Condition<br />
Material Type<br />
Depth of Cut<br />
Width of Cut<br />
Spindle Speed<br />
Feed<br />
Series 106M 6mm Series 106M 6mm<br />
.2362 .2362<br />
UNCOATED<br />
ISO 4957S5H5653<br />
M4 @ 64 HRc<br />
Ti-NAMITE-A<br />
ISO 4957S5H5653<br />
M4 @ 64 HRc<br />
15 mm 15 mm<br />
.519” .519”<br />
6 mm 6 mm<br />
.2362” .2362”<br />
9 m/min. 9m/min.<br />
477 rpm 477 rpm<br />
25.4 mm/min. 25.4 mm/min.<br />
1 IPM 1 IPM<br />
NUMBER OF HOLES<br />
20<br />
18<br />
16<br />
14<br />
12<br />
10<br />
8<br />
6<br />
4<br />
2<br />
0<br />
HOLES PRODUCED BY UNCOATED AND Ti-NAMITE-A<br />
SERIES 106M DRILLS<br />
UNCOATED<br />
(TOOL FAILURE)<br />
Ti-NAMITE-A COATED<br />
50<br />
SGS HIGH PERFORMANCE