FormulationHIGH SOLIDS THERMOSETTING POLYESTER MELAMINEGRINDBAKING ENAMEL WITH HALOX 550 WF% Wt ClassFormula ConstantsAdd the following in order listed while mixing.POLYMAC HS 57-5776 17.65 ResinNACURE X49-110 0.88 Curing Agentn-Butyl Alcohol [1] 3.54 SolventEastman PM Acetate [1] 3.54 SolventTiona RCL-535 [2] 4.04 Ti DioxideBayferrox 120M [3] 4.04 PigmentSparmite Barytes [4] 26.22 BarytesHALOX 550 WF [5] 2.04 InhibitorHigh speed disperse to 6+ NS Hegman grind.LETDOWNAdd slowly while mixing.POLYMAC HS 57-5776 21.15 ResinCymel 303 [6] 10.98 ResinModaflow 2100 [6] 0.45 SurfactantEastman PM Acetate [1] 5.47 SolventTOTAL100.00Density (g/L)Weight Pigment (%)Volume Pigment (%)Weight Solids (%)Volume Solids (%)PVC (%)VOC (g/L)Formula PropertiesFlash 5-10 min at RTBake at 300 F for 20 minCure at RT, 24 hrs b4testingViscosity - Stormer (KU)@ 25°C1452.9234.2911.2279.8668.5845.83194.7088 - 92 Krebs UnitsSupplier Key[1] Eastman Chemical Company[2] Millennium Inorganic Chemicals[3] Bayer Corporation[4] Elementis Pigments Inc.[5] HALOX[6] CYTECThe information contained herein is correct to the best of our knowledge, but is intended only as a source of information. Therecommendations or suggestions herein are made without guarantee of representation as to results, and we suggest that youevaluate the recommendations contained in this formulation in your own laboratory prior to use.57-5776/550 WF2009-03-09HALOX® 1326 Summer St., Hammond, IN 46320, USAtel: 219.933.1560, www.halox.com

Salt Spray – CRS – 264 hrs – 24mils 2.4 (60 µm)Wayncor 226 550 WF 550 430/650Wayncor 226 550 WF 550 430/6509.7% 2% 2% 7%/0.5%

Salt Spray –CRS– 312 hrs –2.4 mils (60 µm)CROSS‐HATCH &SPATULA ADHESION TESTSWayncor 226 550 WF 550 430/6509.7% 2% 2% 7%/0.5%

Salt Spray –HDG– 312 hrs –2.4 mils (60 µm)CROSS‐HATCH &SPATULA ADHESION TESTSWayncor 226 550 WF 550 430/6509.7% 2% 2% 7%/0.5%