VII. Hot-rolled sheet<br />
Lieferprogramm <strong>EMW</strong> delivery range der <strong>EMW</strong> Coils Spaltband Slit strip Formate Cut-to-size / Zuschnitte sheet<br />
Dicken Thicknesses ab from 1,00 1.00 – 4,00 – 4.50 mm mm ab from 1,00 1.00 – 4,50 – 4.50 mm mm from ab 1,00 1.00 – – 3,00 3.00 mm<br />
Breiten Widths bis up to 1.850 1,850 mm mm bis up to 1.850 1,850 mm mm up bis to 1.530 1,530 mm bis up to 1.850 1,850 mm mm<br />
Lengths Längen --- --- --- up bis to 8,000 8.000 mm up bis to 3.000 3,000 mm mm<br />
Tolerances Toleranzen Tolerances Toleranzen <strong>for</strong> für strips Bänder and <strong>und</strong> sheets: Bleche: DIN DIN EN EN 10051. Finer Engere tolerances Toleranzen and special <strong>und</strong> besondere edge <strong>for</strong>mation Kantenausbildung available by nach arrangement. Absprache<br />
Mild grades – continuously hot-rolled strip and sheet <strong>of</strong> mild steels <strong>for</strong> cold <strong>for</strong>ming acc. to DIN EN 10111 : 2008<br />
Steel grade/type Melt analysis chem. composition Mechanical properties (lat.)<br />
1)<br />
ReL R m Min. fracture elongation<br />
L O = 80 mm L O = 5.65 √S O<br />
C Mn P S 1.0 mm ≤ e 2.0 mm ≤ e 1.0 mm ≤ e 1.5 mm ≤ e 2.0 mm ≤ e 3.0 mm ≤ e<br />
e < 2.0 mm e < 4.5 mm max. e < 1.5 mm e < 2.0 mm e < 3.0 mm e < 4.5 mm<br />
Code Material no. max. % max. % max. % max. % N/mm 2 N/mm 2 N/mm 2 % % % %<br />
DD11 1.0332 0.12 0.60 0.045 0.045 170 – 360 170 – 340 440 22 23 24 28<br />
DD12 1.0398 0.10 0.45 0.035 0.035 170 – 340 170 – 320 420 24 25 26 30<br />
DD13 1.0335 0.08 0.40 0.030 0.030 170 – 330 170 – 310 400 27 28 29 33<br />
DD14 1.0389 0.08 0.35 0.025 0.025 170 – 310 170 – 290 380 30 31 32 36<br />
1) If the product has no pronounced yield point, Rp0.2 must be used instead <strong>of</strong> R eL.<br />
Microalloyed grades – hot-rolled flat products <strong>of</strong> steels with high yield point <strong>for</strong> cold <strong>for</strong>ming acc. to DIN EN 10149 : 1995<br />
Mechanical properties <strong>of</strong> thermo-mechanically rolled steels (long.)<br />
Steel grade/type Upper yield point Tensile strength Fracture elongation, A 1)<br />
1)<br />
ReH 1)<br />
Rm % min.<br />
N/mm 2 min N/mm 2 nominal thickness in mm<br />
< 3 ≥ 3<br />
Code Material no. L O = 80 mm L O = 5.65 √S O<br />
S315MC 1.0972 315 390 – 510 20 24<br />
S355MC 1.0976 355 430 – 550 19 23<br />
S420MC 1.0980 420 480 – 620 16 19<br />
S460MC 1.0982 460 520 – 670 14 17<br />
S500MC 1.0984 500 550 – 700 12 14<br />
S550MC 1.0986 550 600 – 760 12 14<br />
S600MC 1.8969 600 650 – 820 11 13<br />
S650MC 1.8976 650 700 – 880 10 12<br />
S700MC 1.8974 700 750 – 950 10 12<br />
Chemical composition/melt analysis) <strong>of</strong> thermo-mechanically rolled steels<br />
Steel grade/type C Mn Si P S Altotal Nb V Ti Mo B<br />
% % % % % % % % % % %<br />
Code Material no. max. max. max. max. max. min. max. 2)<br />
max. 2)<br />
max. 2)<br />
max. max.<br />
S315MC 1.0972 0.12 1.30 0.50 0.025 0.020 0.015 0.09 0.20 0.15 – –<br />
S355MC 1.0976 0.12 1.50 0.50 0.025 0.020 0.015 0.09 0.20 0.15 – –<br />
S420MC 1.0980 0.12 1.60 0.50 0.025 0.015 0.015 0.09 0.20 0.15 – –<br />
S460MC 1.0982 0.12 1.60 0.50 0.025 0.015 0.015 0.09 0.20 0.15 – –<br />
S500MC 1.0984 0.12 1.70 0.50 0.025 0.015 0.015 0.09 0.20 0.15 – –<br />
S550MC 1.0986 0.12 1.80 0.50 0.025 0.015 0.015 0.09 0.20 0.15 – –<br />
S600MC 1.8969 0.12 1.90 0.50 0.025 0.015 0.015 0.09 0.20 0.22 0.50 0.005<br />
S650MC 1.8976 0.12 2.00 0.60 0.025 0.015 0.015 0.09 0.20 0.22 0.50 0.005<br />
S700MC 1.8974 0.12 2.10 0.60 0.025 0.015 0.015 0.09 0.20 0.22 0.50 0.005<br />
1) <strong>The</strong> values <strong>for</strong> the tensile test are those determined <strong>for</strong> longitudinal samples.<br />
2) <strong>The</strong> sum <strong>of</strong> Nb, V and Ti must not exceed 0.22 %.