Laboratory Tests - KD Feddersen Holding GmbH
Laboratory Tests - KD Feddersen Holding GmbH
Laboratory Tests - KD Feddersen Holding GmbH
Create successful ePaper yourself
Turn your PDF publications into a flip-book with our unique Google optimized e-Paper software.
AKRO-PLASTIC <strong>GmbH</strong><br />
Stand: 02/2007<br />
AKRO-PLASTIC <strong>GmbH</strong><br />
Ein Unternehmen der <strong>Feddersen</strong>-Gruppe<br />
<strong>Laboratory</strong> <strong>Tests</strong><br />
A c c r e d i t e d L a b o r a t o r y<br />
D I N E N I S O / I E C 1 7 0 2 5<br />
D A C - PL- 0 3 7 3 - 05- 00<br />
AKRO-PLASTIC <strong>GmbH</strong><br />
Industriegebiet Brohltal-Ost / Im Stiefelfeld 1 · 56651 Niederzissen<br />
P.O.B. 67 · 56649 Niederzissen<br />
Geschäftsführer: Andreas Stuber, Karlheinz Schuster<br />
Aufsichtsratsvorsitzender: Dr. Matthias von Rönn<br />
Amtsgericht Koblenz HRB 12227<br />
Ein Unternehmen der <strong>Feddersen</strong>-Gruppe<br />
Telefon: +49 2636 9742-0<br />
Telefax: +49 2636 9742-31<br />
info@akro-plastic.com<br />
www.akro-plastic.com<br />
USt-/VAT-IdNr. DE 811117257
Page: 2 von 2<br />
Pos. Test Unit Norm<br />
General properties<br />
1 Density g/cm³ ISO 1183<br />
2 Humidity % ISO 62 r.F.<br />
3 Determintion of GF-length - 34.08.25<br />
4 Pellet weight g/100 Gran. 35.08.39<br />
5 Pellet size mm 35.08.22<br />
7 Residual humidity % DIN EN ISO 15512 Verf. B<br />
8 Bulk density g/l In Anl. an DIN 53 466<br />
9 Injection molding (plaques/specimens) St. -<br />
10 Fines mg/kg 35.08.42<br />
11 Ingredient level % V170/0182<br />
12 Mold shrinkage % 35.08.21<br />
13 Water absorption % ISO 62<br />
14 FTIR-Spectroscopy - -<br />
Mechanical properties<br />
15 Charpy notched impact strength kJ/m² ISO 179 ks<br />
16 Charpy impact strength kJ/m² ISO 179<br />
17 IZOD notched impact strength kJ/m² ISO 180 An<br />
18 IZOD impact strength kJ/m² ISO 180 U An<br />
19 Shore-A-hardness - DIN EN ISO 868<br />
20 Shore-D-hardness - DIN EN ISO 868<br />
Tensile testing (Pos. 21 or 22-25)<br />
21 Nominal tensile stress % ISO 527-2<br />
22 Elongation at yield % ISO 527-2<br />
23 Tensile stress at yield MPa ISO 527-2<br />
24 Tensile modulus MPa ISO 527-2<br />
25 Tensile strength MPa ISO 527-2<br />
26 Elongation at break % ISO 527-2<br />
27 Tensile stress at break MPa ISO 527-2<br />
Thermal properties<br />
28 DSC-Melting point<br />
°C DIN EN ISO 11357<br />
First heating<br />
29 DSC-Melting point<br />
°C DIN EN ISO 11357<br />
Second heating<br />
30 DSC-Crystallisation point °C DIN EN ISO 11357<br />
31 Carbon black content % 35.08.29<br />
32 Ash content % ISO 1172<br />
33 Thermogravimetry °C EN 11358<br />
35 VICAT B50 °C ISO 306<br />
36 Heatresistance HDT/A °C ISO 75-A<br />
37 Heatresistance HDT/B °C ISO 75-B<br />
Accredited test methods according to DIN EN ISO/IEC 17025 are written in red
Page: 3 von 3<br />
Pos. Test Unit Norm<br />
Rheological properties<br />
38 MFR g/10 min ISO 1133 MFR<br />
39 MVR cm³/10 min ISO 1133 MVR<br />
40 Viscosity number PA ml/g ISO 307 PA<br />
41 Viscosity number PET/PBT ml/g DIN 1628-5<br />
Optical properties<br />
42 Black Specks - 36.08.04<br />
43 Dirt-Index - 36.08.04<br />
44 Color L* - 35.08.12<br />
45 Color a* - 35.08.12<br />
46 Color b* - 35.08.12<br />
47 Color delta a - 35.08.12<br />
48 Color delta b - 35.08.12<br />
49 Color delta E - 35.08.12<br />
50 Color delta L - 35.08.12<br />
51 Yellowness index - 35.08.12<br />
52 Visual inspection of color - 35.08.12<br />
53 Identification and contamination - 35.08.12<br />
54 Contamination SP/kg 35.08.16<br />
55 Size of carbon black agglomerate µm 35.08.25-0<br />
Electrical properties<br />
57 Volume resistivity x cm IEC 60093-1<br />
58 Surface resistivity IEC 60093<br />
Flammability<br />
59 Flammability UL 94 class 35.08.13<br />
60 Flammability UL 94 HB class 35.08.14<br />
61 Rate acc. FMVSS 302 (