WEICON Easy-Mix PE-PP Construction Adhesive - Weicon.com
WEICON Easy-Mix PE-PP Construction Adhesive - Weicon.com
WEICON Easy-Mix PE-PP Construction Adhesive - Weicon.com
Create successful ePaper yourself
Turn your PDF publications into a flip-book with our unique Google optimized e-Paper software.
Technical data<br />
Basis:<br />
Condition/Nature:<br />
Supplied in:<br />
Content:<br />
<strong>WEICON</strong> <strong>Easy</strong>-<strong>Mix</strong> <strong>PE</strong>-<strong>PP</strong> 45 in liquid condition<br />
Methylmethacrylate<br />
pasty<br />
double cartridge<br />
38 ml<br />
<strong>Mix</strong>ing proportion by volume resin / hardener: 10 : 1<br />
Pot life with 10 ml material and at +20°C (+68°F):<br />
Density of the mixture:<br />
Viscosity of the mixture at + 20°C (+68°) Brookfield:<br />
Temperature:<br />
Colour before curing:<br />
Bonding gap:<br />
Cure time at + 20°C (+68°F)<br />
Processing, optimum:<br />
Curing:<br />
Optimum:<br />
Maximum:<br />
Handling strength<br />
(35% strength) after:<br />
Mechanical loads<br />
(50% strength) after:<br />
Final strength<br />
(100% strength) after:<br />
<strong>WEICON</strong> <strong>Easy</strong>-<strong>Mix</strong> <strong>PE</strong>-<strong>PP</strong> 45 in cured condition<br />
2 - 3 minutes<br />
1.07 g/cm³<br />
45,000 mPa.s<br />
+20°C to +25°C (+68°F to +77°F)<br />
+15°C to +70°C (+59°F to +158°F)<br />
colourless, translucent<br />
0.2 - 0.3 mm<br />
1.0 mm<br />
2-3 hours (<strong>PP</strong>-<strong>PP</strong>)<br />
6 hours (Alu-Alu)<br />
3-4 hours (<strong>PP</strong>-<strong>PP</strong>)<br />
24 hours (Alu-Alu)<br />
24 hours (<strong>PP</strong>-<strong>PP</strong>)<br />
72 hours (Alu-Alu)<br />
Average strength of the pure Shore hardness D: 55<br />
MMA adhesive in accordance<br />
Tensile strength:<br />
13 MPa<br />
with DIN 53281-83 Max. expansion: 5.3 %<br />
Colour after curing:<br />
yellowish, transparent<br />
ABS:<br />
10.5 N/mm²<br />
GFK:<br />
17.0 N/mm²<br />
GFK Gelcoat:<br />
10.1 N/mm²<br />
HD<strong>PE</strong>:<br />
7.6 N/mm²<br />
PA 6.6 (30% glass fibre particles):<br />
5.7 N/mm²<br />
PC:<br />
5.9 N/mm²<br />
<strong>PE</strong> HD (high density):<br />
7.4 N/mm²<br />
<strong>PE</strong> LD (low density):<br />
2.8 N/mm²<br />
<strong>PE</strong> UHMW (ultrahigh molecular):<br />
5.2 N/mm²<br />
PMMA:<br />
6.6 N/mm²<br />
<strong>PP</strong>:<br />
7.6 N/mm²<br />
PS:<br />
5.3 N/mm²<br />
PVC:<br />
14.1 N/mm²<br />
Aluminium:<br />
15.7 N/mm²<br />
Glass:<br />
4.5 N/mm²<br />
Copper:<br />
15.7 N/mm²<br />
Bright steel:<br />
17.2 N/mm²<br />
Steel, slightly oiled<br />
14.8 N/mm²<br />
VA steel:<br />
15.9 N/mm²<br />
Peel strength at +20°C (+68°F) (HD<strong>PE</strong>):<br />
2.9 N/mm<br />
Temperature resistance:<br />
-50°C to +80°C (-58°F to +176°F)<br />
Thermo forming resistance:<br />
+35°C (+95°F)<br />
Coefficient of thermal below T G<br />
(