CNC Brochure - Solid Concepts
CNC Brochure - Solid Concepts
CNC Brochure - Solid Concepts
Create successful ePaper yourself
Turn your PDF publications into a flip-book with our unique Google optimized e-Paper software.
Coefficient<br />
of Friction<br />
Heat Deflection<br />
Heat Deflection<br />
Flexural Strength<br />
Flexural Modulus<br />
40 psi, 50 fpm<br />
Temp. @ 66 psi<br />
Temp. @ 264 psi Dielectric Strength Flammability UL 94<br />
—<br />
300,000 psi<br />
(2,000 MPa)<br />
—<br />
201˚F<br />
(94˚C)<br />
—<br />
—<br />
—<br />
14,000 psi<br />
(98 MPa)<br />
340,000 psi<br />
(2,300 MPa)<br />
0.38<br />
280˚F<br />
(138˚C)<br />
270˚F<br />
(132˚C)<br />
380 V/mil<br />
UL 94 HB<br />
19,000 psi<br />
(131 MPa)<br />
798,000 psi<br />
(5,500 MPa)<br />
0.22<br />
298˚F<br />
(147˚C)<br />
295˚F<br />
(146˚C)<br />
490 V/mil<br />
—<br />
15,500 psi<br />
(107 MPa)<br />
440,000 psi<br />
(3,000 MPa)<br />
0.26<br />
455˚F<br />
(235˚C)<br />
194˚F<br />
(90˚C)<br />
300-400 V/mil<br />
V-2 (3.0 mm)<br />
18,500 psi<br />
(128 MPa)<br />
550,000 psi<br />
(3,800 MPa)<br />
—<br />
490˚F<br />
(254˚C)<br />
482˚F<br />
(253˚C)<br />
—<br />
—<br />
11,500 psi<br />
(79 MPa)<br />
420,000 psi<br />
(2,900 MPa)<br />
0.20<br />
336˚F<br />
(169˚C)<br />
257˚F<br />
(125˚C)<br />
500 V/mil<br />
HB (1.47)<br />
—<br />
225,000 psi<br />
(1,550 MPa)<br />
—<br />
172˚F<br />
(78˚C)<br />
—<br />
—<br />
—<br />
—<br />
225,000 psi<br />
(1,550 MPa)<br />
—<br />
—<br />
—<br />
—<br />
—<br />
15,000 psi<br />
(105 MPa)<br />
475,000 psi<br />
(3,275 MPa)<br />
—<br />
230˚F<br />
(110˚C)<br />
203˚F<br />
(95˚C)<br />
—<br />
UL 94 HB<br />
481,000 psi<br />
(3,300 MPa)<br />
—<br />
179˚F<br />
(82˚C)<br />
176˚F<br />
(86˚C)<br />
544 V/mil<br />
UL 94 V-O<br />
—<br />
480,000 psi<br />
(3,300 MPa)<br />
—<br />
165˚F<br />
(74˚C)<br />
154˚F<br />
(68˚C)<br />
—<br />
UL 94 V-O<br />
30,000 psi<br />
(207 MPa)<br />
1,400,000 psi<br />
(9,650 MPa)<br />
0.20<br />
—<br />
530˚F<br />
(276˚C)<br />
1.4 x 10-5<br />
ohm-cm<br />
—<br />
22,000 psi<br />
(152 MPa)<br />
480,000 psi<br />
(3,300 MPa)<br />
—<br />
410˚F<br />
(210˚C)<br />
392˚F<br />
(200˚C)<br />
710 V/mil<br />
UL 94 V-O<br />
30,000 psi<br />
(207 MPa)<br />
9,000,000 psi<br />
(6,200 MPa)<br />
—<br />
410˚F<br />
(210˚C)<br />
408˚F<br />
(209˚C)<br />
670 V/mil<br />
UL 94 V-O<br />
65,000 psi<br />
(450 MPa)<br />
2,900 psi<br />
(20 MPa)<br />
—<br />
—<br />
—<br />
800 V/mil<br />
UL 94 V-O<br />
Note: Material properties are for<br />
reference purpose only. Actual values<br />
may vary as they are affected by part<br />
geometry and process parameters.<br />
SOLIDCONCEPTS.COM