Conclusion<br />
Hostanox ® * P-<strong>EPQ</strong> ® has to be considered<br />
as the additive of choice in<br />
applications of polypropylene where<br />
superior stabilization is required.<br />
Particularly in clarified or nucleated<br />
polypropylene, the use of Hostanox<br />
P-<strong>EPQ</strong> safeguards excellent melt and<br />
color stability during processing of<br />
the resin.<br />
6<br />
Experimental<br />
Third-generation polypropylene random<br />
copolymer was melt compounded<br />
with the respective additive formulations.<br />
The following base stabilization<br />
(BS) was used: 0.1 % calcium<br />
stearate plus 0.05 % AO-2. Processing<br />
stabilizers (PS) were applied at 0.1 %<br />
and nucleating agents (NA) at a level<br />
of 0.25 %.<br />
Preparation of the Samples<br />
Additives were dry blended with the<br />
polymer and pre-extruded at 210 °C.<br />
Multiple extrusions were carried out<br />
on a single screw laboratory extruder<br />
(compression ratio 1:3, L:D = 25, 50<br />
rpm). The strand was chilled in water<br />
and pelletized. These samples were<br />
used for MFR characterization, reprocessing<br />
and for injection molding<br />
into 100 x 100 x 1 mm3 plaques on<br />
an Arburg Allrounder 221-75-350 at<br />
245 °C.