Leghe universali Universal alloys<br />
KERAMIT BIO LF 1, 2, 3, 6, 7, 9<br />
KERAMIT PERFORMANCE 1, 2, 3, 6, 7, 8, 9<br />
KERAMIT LF 1, 2, 3, 6, 7, 9<br />
KERAMIT PRESS LF 1, 2, 3, 6, 7, 8, 9<br />
ILOR KERAMIT LF 1, 2, 3, 6, 7, 8, 9<br />
KERAMIT ECO LF 1, 2, 3, 6, 7, 8, 9<br />
KERAMIT 300 LF 1, 2, 3, 6, 7, 9<br />
PAL KERAMIT LF PRESS 1, 2, 3, 6, 7, 8, 9<br />
PAL KERAMIT LF 1, 2, 3, 6, 7, 8, 9<br />
KERAMIT PRESS LF ECO 1, 2, 3, 6, 7, 8, 9<br />
Leghe Universali<br />
Universal Alloys<br />
Tecnologie Sintercast<br />
Sintercast Technologies<br />
SINTERCAST GOLD 1, 2, 3, 7, 9<br />
SINTERCAST PLUS 1, 2, 3, 7, 9<br />
LEGENDA / LEGEND<br />
1 = Intarsi occlusali/ One surface inlays<br />
2 = Intarsi MO/ One and two surface inlays<br />
3 = Corone 3/4, onlay, ponti poco estesi/ 3/4 crowns, onlays, short bridges<br />
4 = Scheletrati/ Partial dentures<br />
5 = Barre e corone telescopiche/ Bars and telescopic crowns<br />
6 = Fresaggi/ Milling<br />
7 = Corone e ponti poco estesi (ceramica)/ Crowns and short bridges (PFM)<br />
8 = Corone e ponti estesi (ceramica)/ Crowns and long bridges (PFM)<br />
9 = Per ceramiche LFC - Alta espansione/ For low fusing - High expansion ceramics<br />
10 = Ganci/ Clasps<br />
11 = Corone complete/ Complete crowns<br />
Le leghe sono disponibili anche in formato Laser Weld in strisce e fili.<br />
Per ulteriori informazioni consultare la tabella metallografica.<br />
The alloys are available in Laser Weld shape (wire and strip). For any<br />
other information please see the alloys and solders table.<br />
Str. S. Rocco, 28 - 14018 Villafranca d’Asti - Asti - Italy<br />
tel. +39.0141.933811 - fax +39.0141.943840<br />
e-mail: export@nobilmetal.it - contact@nobilmetal.it - http://www.nobilmetal.it<br />
A.S. <strong>0509MAT29CHE007</strong> - rev.00 - 10/2008<br />
indicate per ceramiche LF ad alta espansione, resine e compositi<br />
indicated for high expansion LF porcelains, resins and composites
dati tecnici technical data<br />
corrosione e citocompatibilità corrosion and cytocompatibility<br />
Leghe universali<br />
Universal alloys<br />
Intervallo<br />
fusione<br />
Melting<br />
range<br />
°C<br />
Temperatura<br />
colata<br />
Casting<br />
temperature<br />
°C<br />
Temperatura<br />
preriscaldo<br />
Burn-out<br />
temperature<br />
°C<br />
C.E.T.<br />
T.E.C.<br />
25-500°C<br />
25-600°C<br />
Adesione<br />
Adhesion<br />
Modulo<br />
elastico<br />
Modulus of<br />
elasticity<br />
GPa<br />
Limite<br />
elastico<br />
Yield strength<br />
MPa<br />
Allungamento<br />
Elongation<br />
%<br />
Carico<br />
di rottura<br />
Tensile<br />
strength<br />
MPa<br />
D<br />
Durezza<br />
Vickers<br />
Vickers<br />
hardness<br />
HV 5/30<br />
C Q E D<br />
E E E<br />
Leghe universali<br />
Universal alloys<br />
Corrosione Corrosion<br />
M<br />
Citocompatibilità<br />
E ocp<br />
E I p 300 I Cytocompatibility<br />
p<br />
N<br />
composizione composition<br />
Leghe universali<br />
Universal alloys<br />
Au<br />
%<br />
Pt<br />
%<br />
Pd<br />
%<br />
Ag<br />
%<br />
Cu<br />
%<br />
KERAMIT BIO LF 73,0 9,6 - 13,7 - - 2,0 - - Ir, Rh, Ta, Fe 83,5 Y 16,2<br />
KERAMIT PERFORMANCE 72,2 9,0 - 15,0 - - 2,4 - - Ir, Rh, Ta, Fe 82,0 Y 16,1<br />
KERAMIT LF 72,0 9,0 - 11,2 4,8 1,0 1,9 - - Ir 81,1 Y 16,5<br />
KERAMIT PRESS LF 64,0 2,0 10,6 20,0 - 1,0 2,0 - - Ir, Fe 76,8 Y 15,1<br />
In<br />
%<br />
Zn<br />
%<br />
Sn<br />
%<br />
Ga<br />
%<br />
Altri<br />
Others<br />
Au &<br />
PGM<br />
%<br />
Colore<br />
Colour<br />
B<br />
Densità<br />
Density<br />
g/cm 3<br />
s h s h s h s sh h<br />
KERAMIT BIO LF 990-1090 1190 730 15,7 16,1 31,11 94 360-490 11-8 440-560 160-185-200<br />
KERAMIT PERFORMANCE 980-1075 1190 730 16,2 16,6 31,17 98 315-380 16-11 420-540 165-180-200<br />
KERAMIT LF 950-1040 1190 730 16,0 16,2 31,4 97 350-520 15-8 550-670 175-200-235<br />
KERAMIT PRESS LF 1135-1225 1350 800 15,9 16,3 45,29 95 265-480 24-12 380-610 160-205-225<br />
ILOR KERAMIT LF 935-1015 1200 700 16,3 16,6 46,71 108 340-385 10-6 405-500 205-240-260<br />
KERAMIT ECO LF 1065-1165 1290 800 16,5 16,8 27,68 101 260-530 20-16 380-600 155-230-250<br />
KERAMIT 300 LF 1030-1110 1250 800 16,6 17,0 46,71 90 370-450 5-3 550-615 200-210-220<br />
PAL KERAMIT LF PRESS 1160-1230 1370 820 15,8 16,1 41,71 115 385-470 18-10 685-700 200-215-220<br />
PAL KERAMIT LF 1070-1140 1280 800 15,9 16,2 64,47 100 300-580 20-8 570-790 155-220-250<br />
KERAMIT PRESS LF ECO 1090-1190 1340 800 16,5 16,9 45,51 105 420-470 12-10 620-650 190-210-220<br />
KERAMIT BIO LF 80 725 0,44 9,7 0<br />
KERAMIT PERFORMANCE 66 875 0,43 8,36 0<br />
KERAMIT LF 86 750 0,176 3,99 0<br />
KERAMIT PRESS LF 85 750 1,5 30,0 0<br />
ILOR KERAMIT LF 55 750 0,52 7,6 0<br />
KERAMIT ECO LF 100 730 0,354 8,36 0<br />
KERAMIT 300 LF 35 450 6,17 11,36 0<br />
PAL KERAMIT LF PRESS 59 460 0,403 4,6 0<br />
PAL KERAMIT LF 39 580 0,48 8,5 0<br />
KERAMIT PRESS LF ECO 62 370 6,9 8,93 0<br />
Tecnologie Sintercast Sintercast Technologies<br />
ILOR KERAMIT LF 59,0 11,5 2,0 20,8 - 3,5 3,0 - - Ir 72,7 Y 14,9<br />
KERAMIT ECO LF 57,0 - 10,6 29,2 - 3,0 - - - Ir 67,8 Y 14,2<br />
KERAMIT 300 LF 30,0 2,0 21,1 36,0 - 10,5 - - - Ru, Fe 53,2 Y 12,2<br />
PAL KERAMIT LF PRESS - - 47,8 43,8 - - - 8,2 - Ru 48,0 W 10,9<br />
PAL KERAMIT LF - - 39,8 51,8 - 2,1 4,0 2,1 - Ru 40,0 W 10,6<br />
KERAMIT PRESS LF ECO - - 37,8 55,5 - 0,5 3,5 2,5 - Ru 37,9 W 10,8<br />
Tecnologie Sintercast Sintercast Technologies<br />
SINTERCAST GOLD 99,99 - - - - - - - - X 99,99 Y 19,3<br />
SINTERCAST PLUS 95,0 5,0 - - - - - - - - 100,0 Y 19,5<br />
ISO 9693:1999<br />
ISO 22674:2004<br />
B<br />
Y = giallo W = bianco<br />
yellow white<br />
Tecnologie Sintercast Sintercast Technologies<br />
SINTERCAST GOLD 1060-1075 - - 14,2 14,6 - - - - - 90-95<br />
SINTERCAST PLUS 1085-1160 - - 14,3 14,5 - - - - - 90-95<br />
C = 10 -6 . K -1<br />
D = MPa = N/mm 2<br />
GPa = K . N/mm 2<br />
E = s = stemprato/ softened<br />
sh = auto-temprato/ self-hardened<br />
h = temprato/ hardened<br />
Ps (HV4/30) = dopo sinterizzazione/ after sintering<br />
Af (HV4/30) = dopo cottura/ after firing<br />
Q = Test per l’adesione metallo-ceramica (Schwickerat Crack<br />
Initiation Test) secondo la Normativa ISO 9693:1999/ Test<br />
for metal-ceramic adhesion (Schwickerat Crack Initiation<br />
Test) in accordance with ISO 9693:1999<br />
Ps<br />
Af<br />
SINTERCAST GOLD 205 1080 0,33 8,22 0<br />
SINTERCAST PLUS 158 915 0,11 8,4 0<br />
Le leghe universali Nobil Metal hanno brillantemente superato<br />
i vari test previsti dalle normative tecniche; alcune di esse<br />
sono risultate più performanti, in termini di risultati, rispetto<br />
alle leghe convenzionali per ceramica (PFM).<br />
The universal alloys by Nobil Metal have successfully<br />
passed the tests required by the standards; some alloy<br />
showed better results than PFM conventional ceramic.<br />
M = E ocp<br />
= mV<br />
E p<br />
= mV<br />
I 300<br />
= µA . cm -2<br />
I p<br />
= µA . cm -2<br />
See: EN ISO 10993-5: 99<br />
N = Valore scala/ Scale value<br />
0 = Assenza totale di citotossicità/ Total lack of cytotoxicity<br />
1 = Lieve citotossicità/ Light cytotoxicity<br />
2 = Moderata citotossicità/ Moderate cytotoxicity<br />
3 = Grave citotossicità/ Serious cytotoxicity