Views
1 month ago

SOLID SURFACE SINKS CATALOGUE

Physical Properties

Physical Properties Feature Unit Result Test Take Over Explanation Specific Weight / Density g/cm 1.70 - 1.78 DIN ISO 1183 Instron Tensile Strength psi 5.400 ASTM D 638 Instron Strain Modulus psi 1.4 x 10 ASTM D 638 Instron Elongation at Break % min. 0.85 - 1.15 ASTM D 638 / DIN EN ISO 178 Instron Flexural strength mpA 70 - 92 ASTM D 790 / DIN EN ISO 178 M Commensurable Flexural Modulus MPa 8.400 - 10.500 ASTM D 790 / DIN EN ISO 178 Hardness (Rockwell) hrm 87 - 94 ASTM D 785, M Skalası Thermal Expansion mm/m.C 3.04 x 10 ASTM D 696 Dry Heat Resistance Passing, 4 - Slight Change ISO 19712-2, Chapter 12 Gloss 60 Degrees 5.20 ANS Z 124 Color Durability No Change NEMA LD 3 Fading Test 5, No Change ISO 19712-2, Bölüm 9, Metod A Wear & Cleanability Passing ANS Z 124 Boiling Water Surface Resistance No Change NEMA LD 3 High Temperature Resistance No Change NEMA LD 3 Dry Heat Resistance Geçer, 4 - Slight Change ISO 19712-2, Chapter 12 Stain Retention Passing NEMA LD 3 Stain Resistance Geçer, 4 - Slight Change ISO 19712-2 Bölüm 10.1 Metod A Impact Resistance No Fracture NEMA LD 3 Impact Resistance (Large Diameter Ball) No Fracture ISO 19712-2 Chapter 8 IZOD Impact Strength Ft.Ib/in 0.28 ASTM D 256 Water Absorption % Maks. 0.03 ASTM D 570 Fungi and Bacteria Yok ANS Z 124 Resistance to Weather Conditions No Change ASTM D 1499 Reaction Against Fire B-sl, d0 EN 13501-1 1000 Saat Feature Unit Result Test Take Over Density g/cm³ 1.70 - 1.78 DIN ISO 1183 Bending Modulus MPa 8.400 - 9220 DIN EN ISO 178 Bending Strength MPa 57.1 - 74.0 DIN EN ISO 178 Fracture Point Extension % 0.76 - 0.93 DIN EN ISO 178 Compressive Strength MPa 175 - 178 EN ISO 604 Impact Resistance (Spring Load) N ≥ 25 DIN ISO 4586T11 Impact Resistance (Ball Drop) Cm ≥ 120 DIN ISO 4586T12 Surface Hardness (Mohs Index) 2 - 3 DIN EN 101 Resistance to Surface Wear Mm3/10 Rev 58 - 63 DIN ISO 4586T6 Resistance to Boiling Water - Weight Increase % 0.1.0.3 DIN ISO 4586T7 Resistance to Boiling Water - Surface Increase No Visible Changes DIN ISO 4586T7 Dimensional Stability at 20 ºC % Length Change 0.16 ≤ DIN ISO 4586T10 Resistance to Heat 180 °C 4 - Small Change DIN ISO 4586T8 Light Disease (Xenon Arc) Blue Wool Ölçeği ≤ 6 DIN ISO 4586T16 Resistance to Slide with 100um ̊ Pain 5.8 ° - Passable R9 Conditioned (6 ° Mim) DIN 51130:1992-11 Resistance to Slide with 120um ̊ Pain 7.6 ° - not passable R9 Conditioned (6 ° Mim) DIN 51130:1992-11 Resistance to Slide with 150um ̊ Pain 8.1 ° - not passable R9 Conditioned (6 ° Mim) DIN 51130:1992-11 Bacteria and Fungi Resistance Germs Will Not Permit Uremes DIN EN ISO 846 Electrostatic Surface Behavior Ω 1x10 DIN IEN 61 340-4-1 96

Stain/Residual Cleaning Method 16 Hours Later In case of Any Stain/Residual After 16 Hours Can be cleaned by using "Ajax" cleaning detergent and wet Scotch-Brite sponge It should be polished after sanding by using a sandpaper No. 1200-2000. If it is not cleaned up, it should be sanded and then polished. Petrol Blood Soap Wine Olive Oil Ketchup Tea Grape Juice Coffee Acetone #Asetik Asit (%30) #Amonyum Hidroklorid #Amonyum Hidroksit (%5.28) #Amil Asetat #Amil Alkal #Bady Şartlandırıcı #Tükenmez Kalem #Bleach (Ağartıcı Ev Tipi) #Butil Alkol #Kalsiyum Tiosiyonat (%78) #Karbon Disulfit #Karbon Setraklorit #Sigara #Yemeklik Yaplar #Pamuk Yağı #Kupra Amonyağı #Bulaşık Yıkama Sıvısı #Derz #Etonol (Etil Alkol) #Etil Eter #Formaldehit #Gazalin #Gentiyana Menekşesi #Hidroklorik Asit (%20,30,37) #İyot #Limon Suyu #Dudak Boyası #Civa Krom #Metanol (Metil Alkol) #Metil Etil Keton #Metil Turuncu #Metil Kırmızı (%1) #Metalik Yağ #Hardal #Tırnak Parlatıcı #Naftalin #Normal Hekzan #Zeytinyağı #Kurşun Kalem Ucu #Perklorik Asit #Kalıcı Marker (İşaretleyici) Kalem #Ayakkabı Cilası #Sabunsuz Deterjanlar #Sodyum Sülfat #Sodyum Hidroksit Eriği (%5,10,25,40) #Sodyum Sülfat #Soya Sosu #Sukraz Şekeri #Sülfirik Asit (%25,33,60) #Sülforik Asit (%25,33,60) #Tetrahidrofuran #Taluen #Domates Suyu #Üre (%6) #Ürik Asit #Sirke #Zilen (Ksilen) #Çinko Klorid Cleaning Method in case of Any Substantial Stain/Residual After 16 Hours It should be polished after sanding by using a sandpaper No. 1200-2000. If it is not cleaned up, it should be sanded and then polished. #Asetik Asit (%90.98) #Asit Drenaj Temizleyici #Klorobenzen #Kloroform (%10) #Krom Trioksit Asid #Krozol #Droksan #Etil Aseton #Eşitleme Karışımı (50/50) #Film Geliştirici #Formik Asit (%50.90) #Furfural #Glasial (Saf Asetik) #Hidroflorik Asit (%48) #Luralit Karışımı (50/50) #Nitrik Asit (%25,30,70) #Metri Klorid Esaslı Ürünler (Boya Sökücü, Fırça Yıkayıcı ve Metal #Fenol (%48) #Fosforik Asit #Sülfirik Asit #Triklor Asetik Asit #3M Avagardm D 97

CATALOGUE
Wilsonart HD Sinks Wilsonart Wilsonart Solid Surface Sinks
DuPont™ Solid Surfaces shapes collection
Sinks, Taps & Bathroom Accessories - Mico Design
Roco Catalogue 10 - Joiners Hardware - Sinks ... - Specifile on-line