PRECISION COLD DRAWN SEAMLESS STEEL TUBE

10.Tubes for bearing rings
Production range:
Tolerances
O.D. D < 50 mm:
– 0
+ 0,15 mm
D ≥ 50 mm:
– 0
+ 0,25 mm
W.T. ± 7,5 % (acc. agreement 5 %)
Lengths
3000 ± 500 mm
Straightness
1 mm/1000 mm, max 2,5 mm/3000 mm
Steel quality
DIN 17 230 – 100Cr6
34
10. Lagerrohre
Abmessungsbereich:
Outside diameter Wall thickness
Aussendurchmesser Wanddicke
[mm] [mm]
22–25 3–4,1
25,01–29 3–5
29,01–32 3–6,7
32,01–40 3–7,8
40,01–70 3–8
Grenzabmaße
AD D < 50 mm:
– 0
+ 0,15 mm
D ≥ 50 mm:
– 0
+ 0,25 mm
WD ± 7,5 % (nach der Vereinbarung 5 %)
Längen
3000 ± 500 mm
Geradheit
1 mm/1000 mm, max 2,5 mm/3000 mm
Stahlsorte
DIN 17 230 – 100Cr6
C Mn Si P S Cr Ni Cu Sn
0,90 0,30 0,15 max max 1,30 max max max
1,10 0,50 0,30 0,017 0,015 1,65 0,10 0,15 0,010
Delivery conditions
GKZ + K + G – annealing for globular carbide + cold finished + soft
annealing
Hardness
After soft annealing is 174–220 HB. Dispersion of hardness along the
tube lenght max 15 HB. Hardness by hardening test is min 61 HRc.
Surface condition
The tubes are delivered with surface after soft annealing. Max depth
of defects is 0,25 mm inclusive decarbonizing
Lieferzustand
GKZ + K + G – geglüht auf kugelige Carbide + kalt gezogen
+ weichgeglüht
Härte
Nach dem Weichglühen ist 174–220 HB. Die Ausschläge der Härte
entlang der Rohrlänge sind max. 15 HB. Härte beim Stirnabschreckversuch
ist min. 61 HRc.
Oberflächezustand
Die Rohre werden mit Oberfläche nach Weichglühen geliefert. Max.
Fehlertiefe ist 0,25 mm inclusive Entkohlung.