LFS | SKL skirting trunking systems - OBO Bettermann

Chemical resistances of hard PVCA = very good resistanceB = average resistanceC = not resistantMediumTemp.°CResistanceA = very good resistanceB = average resistanceC = not resistantMediumTemp.°CResistanceFurfuryl alcohol 20 CGelatine 60 AGluconic acid 20 AGlucose 60 AGlutamic acid 20 AGlycerine 60 AGlycine 40 AGlycol 60 AHeptanes 20 AHexachloroethane 20 CHexacyanoferrates-II (Na-) 40 AHexacyanoferrates-III (K-) 40 AHexafluorosilicates (ammonium-, K- and others) 60 AHexafluorosilicic acid 32% 60 AHexamethylenetetramine (urotropine) 40% aqueous 60 AsolutionHumic acids 20 AHydrazine, diluted solution 100% 20 CHydrazine, diluted solution 30% 20 AHydrobromic acid to 40% 60 AHydrochloric acid to 30% 20 AHydrochloric acid to 30% 60 BHydrochloric acid to 37% 20 AHydrochloric acid to 37% 40 BHydrofluoric acid to 40% 40 AHydrofluoric acid to 40% 60 BHydrogen bromide 100% 20 AHydrogen bromide 100% 60 BHydrogen chloride (gaseous, dry and moist) 40 AHydrogen cyanide 40 AHydrogen peroxide to 30% 60 AHydrogen peroxide to 90% 20 AHydrogen sulphide 60 AHydroxides (alkaline-earth metal) 60 AHydroxides (K-, Na-) 60 AHypochlorites (K-, Na- and others) 60 Ahypochlorous acid 60 AIlluminating gas 20 AIodates (K-, Na- and others) 60 AIodides (K-, Na-) 60 AIodine 20 CIsobutylphosphate 20 CPentylalcohol 60 APentylchloride 20 CPerbonate (K-) 60 APerchlorate 40 APerchloric acid 70% 20 APermanganate (K-) 6 to 15% 40 APermanganate (K-) 6 to 15% 60 BPermanganate (K-) to 6% 60 APeroxymonosulphuric acid (Caro's acid) 20 APersulphate (Ammonium-, K-, Na- and others) 40 APetroleum 60 APhenol 1% 20 APhenol 90% 45 BPhenylhydrazine 20 CPhenylhydrazine chloride 20 BPhenylhydrazine chloride 60 CPhosgene, gaseous 20 APhosgene, gaseous 60 BPhosgene, liquid 20 CPhosphates (ammonium-, K-, Na- and others) 60 APhosphoric acid 40 APhosphoric acid 60 BPhosphorus pentoxide 20 APropane 20 APropanol 60 APyridine 20 ARhodanides (ammonium-, K-, Na- and others) 60 ASalicylic acid 20 ASilicates (K-) 20 ASoap solution 40 AStearic acid 60 ASulphates (ammonium-, K-, Na- and others) 60 ASulphites (ammonium-, K-, Na- and others) 60 ASulphur dioxide, gaseous, dry and moist 100% 60 ASulphuric acid to 40% 20 CSulphuric acid to 50% 50 ASulphuric acid to 50% 60 ASulphuric acid to 80% 40 CSulphuric acid to 80% 60 BSulphuric acid to 96% 20 ASulphuric acid to 96% 60 BSulphuric acid, fuming (10% oleum) 20 CSulphurous acid 60 AAdditional informationLactic acid 10% 20 ALactic acid 10% 60 CLactic acid 100% 20 CLard 20 ALinoleic acid 60 ALinseed oil 60 AMalic acid 20 AMaterial characteristicsMethanol 100% 40 AMethanol 100% 60 BMethyl bromide 20 CMethyl chloride 20 CMethyl methacrylate 20 CMethylamine 20 BMethylene dichloride 20 CMilk 20 AMineral oils 60 CN,N-diethyl aniline 20 CNaphthalene 20 CNitrates (ammonium-, K-, Na- and others) 60 ANitric acid 25% 20 ANitric acid 25% 60 BNitric acid 50% 20 ANitric acid 50% 50 BNitric acid 95% 20 CNitrites (K-, Na- and others) 60 ANitrobenzene 20 CNitrogen oxide 20 CNitroglycerine 20 BNitrous acid to 50% 50 ANitrous acid to 98% 20 COleic acid 60 AOxalates (ammonium-, K-, Na- and others) 60 AOxalic acid 40 AOxygen 60 AOzone 10% 30 AOzone 10% 60 BPalmitic acid 20 AParaffin 40 APentyl laurate 20 CPentylacetate 20 CTallow 60 ATan bark 20 ATar, free from aromatic hydrocarbons 20 ATartaric acid 60 ATetraethyl lead 60 ATetrafluoroboric acid 20 ATetrahydrofurane 20 CThickness 60 AToluene 20 ATransformer oil 60 ATrichloroethylene 20 CTurpentine 20 AUrea 60 CVegetable oils 40 AVinyl acetate 20 CViscose spinning solutions 60 AWater 40 AWater 60 BWine 40 AWine vinegar 50 AWood tar 20 CXylenes 20 CMaterial properties of the hard PVC usedMaterial description according to DIN 7748PVC-U-E-D-080-04-28Tensile strength according to DIN 53 455min. 40 N/mm²Elongation at tear according to DIN 53 455 min. 65%Puncture strength according to DIN 53 481min. 20 KV/mmSurface resistance according to DIN 53 482 min. 10 10Thermoforming resistance according to DIN 53 460/B min. 75 °CTemperature resistance in the application max. 65 °CFlammability according to UL 94 Level V-0Hot-wire test according to DIN IEC 695 960 °CMaterial classification to DIN EN 4102, Class B1 and B2-tested06 LFS_Katalog_2010_Neuer_Stand / en / 25/02/2010 (LLExport_00995)80 OBO LFS