Material standard values<br />
Material<br />
TECADUR<br />
PBT GF30<br />
TECAMID<br />
6<br />
TECAM<br />
6 MO<br />
TECAMID<br />
6 GF25<br />
black<br />
TECAMID<br />
6 GF30<br />
black<br />
TECAMID<br />
6 ID<br />
blue<br />
TECAMID<br />
66<br />
TECAMID<br />
66 MH<br />
TECAMID<br />
66 GF30<br />
black<br />
TECAMID<br />
66/X GF50<br />
black<br />
Chemical Designation<br />
PBT PA 6 PA 6 PA 6 PA 6 PA 6 PA 66 PA 66 PA 66 PA 66<br />
Fillers<br />
glass fibres<br />
molybdenum<br />
disulfide<br />
glass fibres glass fibres detectable<br />
filler<br />
molybdenum<br />
disulfide<br />
glass fibres<br />
glass fibres<br />
Density<br />
(DIN EN ISO 1183)<br />
Mechanical properties<br />
Modulus of elasticity (tensile test)<br />
(DIN EN ISO 527-2)<br />
Tensile strength<br />
(DIN EN ISO 527-2)<br />
Tensile strength at yield<br />
(DIN EN ISO 527-2)<br />
Elongation at yield<br />
(DIN EN ISO 527-2)<br />
Elongation at break<br />
(DIN EN ISO 527-2)<br />
Modulus of elasticity (flexural test)<br />
(DIN EN ISO 178)<br />
Flexural strength<br />
(DIN EN ISO 178)<br />
Compression modulus<br />
(EN ISO 604)<br />
Compressive strength (1% / 2 %)<br />
(EN ISO 604)<br />
Impact strength (Charpy)<br />
(DIN EN ISO 179-1eU)<br />
Notched impact strength (Charpy)<br />
(DIN EN ISO 179-1eA)<br />
Ball intendation hardness<br />
(ISO 2039-1)<br />
Thermal properties<br />
Glass transition temperature<br />
(DIN 53765)<br />
Melting temperature<br />
(DIN 53765)<br />
Service temperature,<br />
short term<br />
Service temperature,<br />
long term<br />
Thermal expansion (CLTE),<br />
23 – 60 °C (DIN EN ISO 11359-1;2)<br />
Thermal expansion (CLTE),<br />
23 – 100 °C (DIN EN ISO 11359-1;2)<br />
Specific heat<br />
(ISO 22007-4:2008)<br />
Thermal conductivity<br />
(ISO 22007-4:2008)<br />
Electrical properties<br />
Specific surface resistance<br />
(DIN IEC 60093)<br />
Surface resistance<br />
(DIN IEC 60093)<br />
Miscellaneous data<br />
Water absorption 24 h / 96 h (23 °C)<br />
(DIN EN ISO 62)<br />
Resistance<br />
to hot water / bases<br />
Resistance to weathering<br />
Flammability (UL94)<br />
(DIN IEC 60695-11-10;)<br />
[ g / cm³ ]<br />
[ MPa ]<br />
[ MPa ]<br />
[ MPa ]<br />
[%]<br />
[%]<br />
[ MPa ]<br />
[ MPa ]<br />
[ MPa ]<br />
[ MPa ]<br />
[ kJ / m² ]<br />
[ kJ / m² ]<br />
[ MPa ]<br />
[ °C ]<br />
[ °C ]<br />
[ °C ]<br />
[ °C ]<br />
[ 10 -5 K -1 ]<br />
[ 10 -5 K -1 ]<br />
[ J / (g*K)]<br />
[ W /(m*K)]<br />
[ Ω ]<br />
[ Ω*cm ]<br />
[%]<br />
1.46 1.14 1.14 1.33 1.36 1.24 1.15 1.15 1.34 1.61<br />
3,400 3,300 3,300 5,100 5,700 3,600 3,500 3,200 5,500 8,700<br />
46 79 84 96 98 80 85 84 91 115<br />
46 78 82 96 98 80 84 83 91 115<br />
5 4 5 9 4 4 7 10 8 2<br />
6 130 37 11 5 21 70 40 14 2<br />
3,400 2,900 3,100 4,900 5,200 3,100 3,100 4,700 9,000<br />
78 100 110 143 140 110 114 135 200<br />
2,800 2,700 2,900 3,900 4,200 2,700 2,700 4,100 6,200<br />
20 / 38 24 / 41 17 / 32 21 / 42 21 / 42 20 / 35 20 / 38 25 / 46 28 / 56<br />
37.0 n. b. n. b. 78.0 60.0 n. b. n. b. n. b. 97.0<br />
7.0 5.0 4.0 5.0 5.0<br />
190 155 160 230 232 175 168 216<br />
45 51 49 49 45 47 52 48 78<br />
224 221 220 217 218 220 258 253 254 256<br />
200 160 160 180 180 160 170 170 170 200<br />
110 100 100 100 100 100 100 100 110 130<br />
8 12 8 7 6 11 10 5<br />
10 13 8 8 6 12 10 5<br />
1.2 1.6 1.6 1.4 1.3 1.5 1.5 1.2<br />
0.33 0.37 0.37 0.40 0.41 0.36 0.36 0.39<br />
10 14 10 14 10 14 10 14 10 14 10 13 10 14 10 14 10 14 10 14<br />
10 14 10 14 10 14 10 14 10 14 10 14 10 14 10 14<br />
0.02 / 0.04 0.3 / 0.6 0.3 / 0.6 0.2 / 0.3 0.2 / 0.3 0.3 / 0.6 0.2 / 0.4 0.2 / 0.4 0.1 / 0.2 0.1 / 0.2<br />
- (+) (+) (+) (+) (+) (+) (+) (+) -<br />
- - (+) (+) (+) - - (+) (+) (+)<br />
HB e HB e HB e HB e HB e HB e HB e HB e HB e HB<br />
Appendix<br />
Data generated directly after machining (standard<br />
climate Germany). For polyamides the values strongly<br />
depend on the humidity content.<br />
Test specimen to DIN EN ISO 527-2<br />
+ good resistance<br />
(+) limited resistance<br />
– poor resistance (depending on concen -<br />
tration, time and temperature)<br />
n.b. not broken<br />
n.a. not applicable<br />
(a) Glass transition temperature<br />
testing according to DIN EN ISO 11357<br />
(b) Thermal conductivity testing according to ISO 8302<br />
(c) Thermal conductivity testing according to ASTM E1530<br />
(d) Surface resistance testing according to ASTM D 257<br />
(e) No listing at UL (yellow card). The information might be<br />
taken from resin, stock shape or estimation. Individual<br />
testing regarding application conditions is mandatory.<br />
(f) Thermal expansion (CLTE), 50 – 200 °C<br />
98