<strong>51</strong>-<strong>21</strong>-<strong>11</strong> Application of Protective Treatment to Metal Parts<br />
Manual : <strong>SRM</strong><br />
Selected effectivity :<br />
SOLUTION<br />
FAC<strong>TO</strong>R WHEN YOU<br />
MEASURE IN (mm or cm)<br />
FAC<strong>TO</strong>R WHEN YOU<br />
MEASURE IN (in)<br />
Cadmium alkaline solution 0.488 80<br />
Cadmium acid solution 0.488 80<br />
Table 004 - Specific Plating Factor<br />
- Example: You have to plate an area of 25 cm² (3.875 in²) with cadmium alkaline solution.<br />
The required thickness is 0.015 mm. The correct ampere-hours setting is: 0.488 x 0.015 x<br />
25 = 0.183 ampere-hours<br />
- Example: You have to plate the same area with the same thickness, but you measure in<br />
inches. The thickness is 0.0006 in and the area has the size of 3.87 sq.in Determine the<br />
correct number of ampere-hours as follows: 80 x 0.0006 x 3.87 = 0.183 ampere-hours<br />
4 Inspection<br />
The cadmium deposit must be fine grain, smooth, and free from blisters, pitting, burns and<br />
other defects. Ensure that the cadmium deposit has good adherence to the metal surface.<br />
Check this with an adhesive tape. Put a strip of adhesive tape onto the treated surface and<br />
draw it quickly away. The adhesive tape must be free from cadmium particles.<br />
5 Procedure for non stainless steel<br />
a<br />
b<br />
Remove all grease from the repair area with a clean cloth soaked in trichloroethane<br />
(Material No. <strong>11</strong>-026 ).<br />
When the cleaning agent has evaporated, mask off all areas which are not to be treated.<br />
WARNING: CLEANING AND DEOXIDIZING SOLUTION IS HARMFUL.<br />
c<br />
d<br />
With a prepared tampon apply the cleaning and deoxidizing solution (Item 1 in the<br />
Table of Subsidiary Materials). Do this at cathodic plating polarity (see manufacturer's<br />
instructions) and 10 to 12 volts. Move the tampon in contact and over the surface until<br />
you get a regular clean surface which is free from water breaks. This should take about 5<br />
to 10 seconds per square inch (6.5 cm² (1.007 in²)).<br />
Rinse the area with clean cold running water.<br />
WARNING: CADMIUM ALKALINE SOLUTION IS DANGEROUS.<br />
e<br />
With a prepared tampon apply the cadmium alkaline solution (Item 9 in the Table of<br />
Subsidiary Materials). Do this at cathodic plating polarity and 8 to 12 volts. Move the<br />
tampon in contact with and over the surface until you get the required thickness. You<br />
should move the tampon at a speed of approximately 10 to 38 cm (4 to 15 in) per<br />
second.<br />
NOTE: For unspecified thickness, the deposit must average between 0.015 mm (0.0006<br />
in) and a minimum of 0.01 mm (0.0004 in), refer to Paragraph 2.B.(1).(d).3 .<br />
f<br />
g<br />
Rinse the area with clean cold running water.<br />
Abrade slightly the treated surface with a Scotch-brite pad or aluminum oxide and<br />
cotton wool. It will brighten the cadmium deposit before passivation and improve its<br />
appearance.<br />
WARNING: CADMIUM/ZINC PASSIVATING SOLUTION IS HARMFUL.<br />