Polyurethane finishes > One-pack system It is difficult to produce a flatting effect in one-component polyurethane finishes with wax only. The basic flatting effect is best produced with silica, after which Ceridust 9615 A, Ceridust 6721 or Ceridust 5551 should be added to improve film properties such as handle, scratch resistance and smoothness. > Two-pack system A finer silk-finish effect can be achieved in two-component polyurethane coatings with Ceridust 9615 A, Ceridust 6721 or Ceridust 5551. Film properties such as handle, scratch resistance and smoothness are also enhanced. Guide formulation Desmophen solution (component A) Desmophen ®+ 1300 75 % solution in xylene 32.0 Nitrocellulose chips E 510 1.5 Ethyl acetate 10.4 Butyl acetate 11.0 Methoxypropyl acetate 10.8 Xylol 8.9 Acronal 4L 0.2 Baysilone OL 17 0.2 Parts by weight 75.0 Desmodur solution (component B) Desmodur ®+ IL 14.2 Desmodur L 75 9.4 Xylol 1.4 Parts by weight 25.0 24 Mixing ratio component A:component B 3:1 Binder content approx. 40 % Degree of crosslinking approx. 1 Efflux time at 23 °C, DIN cup 4 mm, DIN 53 211 approx. 20 sec. Drying at room temperature of a 150 µm thick wet film approx. 40 min. Acid-curing paints The quantity of wax and method of incorporation are similar to those described in detail on page 18 dealing with nitrocellulose lacquers. Guide formulation (white, silk-sheen curtain-coating paint) Note: can also be force-dried, e.g. 5 min. 120 °C Stock paint Vialkyd ®+ AM 421/80 IP 23.00 Titanium dioxide RN 59 23.00 Ceridust 9615 A 1.65 Viamin ®+ HF 164/70 IB Collodium wool H 33 45 % solution in 25.00 methylisobutyl ketone 5.70 Dibutyl phthalate 1.00 No air liquid ®+ 0.65 Methoxypropylacetate 1.00 Butyl acetate 10.00 Isopropanol 3.00 Additol VXL 6245 0.30 Xylol 5.70 Parts by weight 100.00 Hardener p-toluene sulphonic acid 0.60 Phosphoric acid butyl ester 0.40 Butanol 9.00 Parts by weight 10.00 Mixing ratio stock paint : hardener 10 : 1 Tack-free drying approx. 15 min. Efflux time at 23 °C, DIN cup 4 mm, DIN 53 211 approx. 40 sec. Guide formulation (colorless silk-sheen paint) Note: Two-pack system with good body for furniture Stock paint Vialkyd AM 421/80 IP 49.40 Viamin HF 164/70 IB 28.30 Additol VXL 6245 0.30 Ceridust 9615 A 1.00 Xylol 16.50 Butyl acetate 4.50 Parts by weight 100.00 Hardener p-toluene sulphonic acid 1.35 Ethanol 8.65 Parts by weight 10.00 Mixing ratio stock paint : hardener 10:1 Tack-free drying approx. 10 min. Efflux time at 23 °C, DIN cup 4 mm, DIN 53 211 approx. 70 sec.
Paints drying by oxidation Waxes are not very suitable as the sole matting agents for oleoresinous and alkyd paints. However they can be used to improve substantially the mar resistance of high-gloss alkyd resin paints. This is done by adding 2 % to 4 % Ceridust 9615 A, Ceridust 6721 or Ceridust 5551, relative to the finished paint. Ceridust 9615 A additionally prevents the formation of a hard sediment. Guide formulation (water-soluble house paint, white, air-drying) I Resydrol ®+ AY 586 w/ 38 WA 64.0 ammonia, 25 % 0.4 Titanium dioxide RN 59 24.0 Additol VXW 4940 0.2 Additol XW 376 0.4 Additol XW 329 0.4 Additol XL 297/100 0.5 II ammonia, 25 % 0.3 deionized water 9.8 Parts by weight 100.0 Preparation: Mix part I in the given sequence, disperse in a bead mill and adjust to the desired viscosity with part II. Aqueous wood laquer for indoor applications A matt silk finish effect can be obtained by using up to 2.0 % Ceridust 5551 or Ceridust 9615 A on total formulation. Guide formulation I Mowilith ® LDM 7460 74.50 water 6.10 II water 1.00 Saniprot ®+ 99-73 0.20 1,2-Propandiol 1.00 AMP 90 0.20 BYK ®+ 348 0.50 Texanol ®+ 1.00 Agitan ®+ 295 0.20 III water 3.60 Tafigel ®+ PUR 40 0.30 Methoxybutanol 2.50 Ceridust 5551 or Ceridust 9615 A 2.00 water 6.90 Parts by weight 100.00 The raw materials have to be mixed in the above described order with a propeller stirrer. To achieve the optimal dispersion Part III should be made the day before and processed afterwards into Part I and II. Positive wax-based wood stain Good positive effect, no floating of, for instance, Remazol dyes after storage at 50 °C. Guide formulation 2 parts Licowax R 21 5 parts Silicon oil 350 cst 5 parts Spindle oil 2 parts Emulsogen ® P are heated to approx. 100 °C and then stirred well while 20 parts water, hot (90-100°C) are added. The hot concentrate is then well stirred, while 66 parts water are added cold. After 12-24 hours, the formulation is again stirred thoroughly. 25
Page 1 and 2: Pigments & Additives Division Coati
Page 4 and 5: Function of waxes Waxes are incorpo
Page 6 and 7: 6 Ceridust TP Ceridust 9322 F Cerid
Page 8 and 9: Product range Waxes and wax micropo
Page 10 and 11: Properties 1) Ester waxes based on
Page 12 and 13: Ester waxes based on crude montan w
Page 14 and 15: Test methods Drop point DIN 51 801/
Page 16 and 17: Table 1 Test results with a paint r
Page 18 and 19: General information on the processi
Page 20 and 21: Ceridust 3910 Ceridust 3910 has ver
Page 22 and 23: UV reactive waxes TP Ceridust 5091,
Page 26 and 27: Wood wax (aqueous) These are unpigm
Page 28 and 29: Safety data Toxicological propertie
Page 30 and 31: Transport and storage Packaging > L
Page 32: Please note This information is bas

Paints and Coatings Auxiliaries for the coating of surfaces - Clariant

You also want an ePaper? Increase the reach of your titles

Delete template?

Save as template?