- Page 1 and 2: University of Leoben Dissertation S
- Page 3: To my family
- Page 8 and 9: VIII
- Page 10 and 11: Abstract fluctuations in the micron
- Page 12 and 13: XII
- Page 14 and 15: Contents D Microstructural investig
- Page 16 and 17: 1 Introduction changes with the dep
- Page 18 and 19: 1 Introduction is the hardness that
- Page 20 and 21: 1 Introduction shallow nanoindentat
- Page 22 and 23: 1 Introduction dentations made with
- Page 24 and 25: Bibliography [19] Knoop F, Peters C
- Page 26 and 27: Bibliography [65] Qu S, Huang Y, Ni
- Page 28 and 29: 2 List of appended papers Paper F M
- Page 30 and 31: A Microstructural investigation of
- Page 32 and 33: A Microstructural investigation of
- Page 34 and 35: A Microstructural investigation of
- Page 36 and 37: A Microstructural investigation of
- Page 38 and 39: A Microstructural investigation of
- Page 40 and 41: A Microstructural investigation of
- Page 42 and 43: A Microstructural investigation of
- Page 44 and 45: A Microstructural investigation of
- Page 47 and 48: [1] Mulhearn TO. J Mech Phys 1959;7
- Page 49 and 50: B The deformation-induced zone belo
- Page 51 and 52: B.3 Results and discussion formed w
- Page 53 and 54: B.3 Results and discussion investig
- Page 55 and 56:
B.3 Results and discussion Figure B
- Page 57 and 58:
B.4 Summary and conclusions Figure
- Page 59:
[1] Gane N, Cox JM. Philos Mag 1970
- Page 62 and 63:
C Where are the geometrically neces
- Page 64 and 65:
C Where are the geometrically neces
- Page 66 and 67:
C Where are the geometrically neces
- Page 68 and 69:
C Where are the geometrically neces
- Page 71:
[1] Gao H, Huang Y. Scripta Mater 2
- Page 74 and 75:
D Microstructural investigation of
- Page 76 and 77:
D Microstructural investigation of
- Page 78 and 79:
D Microstructural investigation of
- Page 80 and 81:
D Microstructural investigation of
- Page 83 and 84:
E Stacking fault energy and indenta
- Page 85 and 86:
ated with the application of a cube
- Page 87 and 88:
applied reduced indentation moduli,
- Page 89 and 90:
sion scanning electron microscope e
- Page 91 and 92:
[1] Seeger A. Z Naturforsch 1954;9a
- Page 93 and 94:
F Indentation across size scales -
- Page 95 and 96:
covered penetration depth thereby r
- Page 97 and 98:
Figure F.1: (a) Hardness as a funct
- Page 99 and 100:
section II is enclosed by the chang
- Page 101:
structure that typical develops at
- Page 104 and 105:
Bibliography to paper F [19] Balint
- Page 106 and 107:
G TEM sample preparation using low
- Page 108 and 109:
G TEM sample preparation using low
- Page 110 and 111:
G TEM sample preparation using low
- Page 113 and 114:
Bibliography to paper G [1] Giannuz