Natté 420 OF = 1% visual comfort<br />
Technical specifications<br />
TECHNICAL SPECIFICATION UNITY STANDARD RESULT<br />
composition Glassfi bre 36% - PVC 64%<br />
openness factor % NBN EN 410 1%<br />
weight g/m 2 NF EN 12127 420<br />
thickness mm ISO 5084 0,54<br />
density<br />
yarn/cm<br />
warp<br />
25<br />
ISO 7211/2<br />
weft 18<br />
colour fastness to artifi cial light ISO 105 B02 >7<br />
tear strength original daN<br />
warp<br />
5,13<br />
ISO 4674-1 method 2<br />
weft 3,3<br />
elongation up to break original %<br />
warp<br />
6,71<br />
ISO 1421<br />
weft 4,46<br />
breaking strength original daN/5 cm<br />
warp<br />
244,1<br />
ISO 1421<br />
weft 190,9<br />
elongation up to break after colour fastness to artifi cial light %<br />
warp<br />
6,65<br />
ISO 1421<br />
weft 4,35<br />
breaking strength after colour fastness to artifi cial light daN/5 cm<br />
warp<br />
243,8<br />
ISO 1421<br />
weft 180<br />
tear strength after climatic chamber -30°C daN<br />
warp<br />
5,19<br />
ISO 4674-1 method 2<br />
weft 3,44<br />
elongation up to break after climatic chamber -30°C %<br />
warp<br />
6,93<br />
ISO 1421<br />
weft 4,02<br />
breaking strength after climatic chamber -30°C daN/5 cm<br />
warp<br />
266,8<br />
ISO 1421<br />
weft 175,8<br />
tear strength after climatic chamber +70°C daN<br />
warp<br />
5,47<br />
ISO 4674-1 method 2<br />
weft 3,59<br />
elongation up to break after climatic chamber +70°C %<br />
warp<br />
6,66<br />
ISO 1421<br />
weft 3,75<br />
breaking strength after climatic chamber +70°C daN/5 cm<br />
warp<br />
244,5<br />
ISO 1421<br />
weft 162,6<br />
France NF P92-503 M1<br />
Italy UNI 9177 Class 1<br />
fi re classifi cation<br />
Germany DIN 4102 B1<br />
UK BS 5867 C<br />
USA NFPA 701 FR<br />
roll length<br />
30 m<br />
cleaning<br />
confection<br />
EASY<br />
with soapy water<br />
by heat, high frequency or ultrasonic welding<br />
from 2012:<br />
roll length all<br />
interior sunscreens<br />
changes from<br />
50m > 30m<br />
rolls<br />
These properties are given as indicative and don’t have any contractual value<br />