MAINTENANCE<br />
BLOCKOUT<br />
Blockout Ruka<br />
D<br />
OF = 0%<br />
block sunlight & insects<br />
Technical specifications<br />
TECHNICAL SPECIFICATION UNITY STANDARD RESULT<br />
composition Polyester 66% - PUR 34%<br />
openness factor % NBN EN 410 0%<br />
weight g/m 2 NF EN 12127 310<br />
thickness mm ISO 5084 0,14<br />
colour fastness to artifi cial light<br />
front<br />
6<br />
ISO 105 B02<br />
back >7<br />
tear strength original daN<br />
warp<br />
1,65<br />
ISO 4674-1 method 2<br />
weft 3,1<br />
elongation up to break original %<br />
warp<br />
26,5<br />
ISO 1421<br />
weft 30<br />
breaking strength original daN/5 cm<br />
warp<br />
125<br />
ISO 1421<br />
weft 165<br />
elongation up to break after colour fastness to artifi cial light %<br />
warp<br />
23,5<br />
ISO 1421<br />
weft 30<br />
breaking strength after colour fastness to artifi cial light daN/5 cm<br />
warp<br />
120<br />
ISO 1421<br />
weft 160<br />
tear strength after climatic chamber -30°C daN<br />
warp<br />
1,5<br />
ISO 4674-1 method 2<br />
weft 2,9<br />
elongation up to break after climatic chamber -30°C %<br />
warp<br />
29,5<br />
ISO 1421<br />
weft 33<br />
breaking strength after climatic chamber -30°C daN/5 cm<br />
warp<br />
135<br />
ISO 1421<br />
weft 170<br />
tear strength after climatic chamber +70°C daN<br />
warp<br />
1,65<br />
ISO 4674-1 method 2<br />
weft 3,2<br />
elongation up to break after climatic chamber +70°C %<br />
warp<br />
28<br />
ISO 1421<br />
weft 28,5<br />
breaking strength after climatic chamber +70°C daN/5 cm<br />
warp<br />
130<br />
ISO 1421<br />
weft 160<br />
France NF P92-503 M1<br />
Italy UNI 9177 Class 1<br />
fi re classifi cation<br />
Germany DIN 4102 B1<br />
UK BS 5867 C<br />
USA NFPA 701 FR<br />
roll length<br />
30 m<br />
cleaning<br />
with soapy water<br />
confection<br />
by heat, high frequency or ultrasonic welding<br />
EASY<br />
These properties are given as indicative and don’t have any contractual value<br />