TECHNICAL SPECIFICATION UNITY STANDARD RESULT<br />
composition Glassfi bre 36% - PVC 64%<br />
openness factor % NBN EN 410 5%<br />
weight g/m 2 NF EN 12127 385<br />
thickness mm ISO 5084 0,35<br />
density<br />
yarn/cm<br />
warp<br />
20<br />
ISO 7211/2<br />
weft 20<br />
colour fastness to artifi cial light ISO 105 B02 >7<br />
tear strength original daN<br />
warp<br />
4,9<br />
ISO 4674-1 method 2<br />
weft 4,7<br />
elongation up to break original %<br />
warp<br />
3,7<br />
ISO 1421<br />
weft 3,2<br />
breaking strength original daN/5 cm<br />
warp<br />
160<br />
ISO 1421<br />
weft 160<br />
elongation up to break after colour fastness to artifi cial light %<br />
warp<br />
3,7<br />
ISO 1421<br />
weft 3<br />
breaking strength after colour fastness to artifi cial light daN/5 cm<br />
warp<br />
150<br />
ISO 1421<br />
weft 160<br />
tear strength after climatic chamber -30°C daN<br />
warp<br />
5,1<br />
ISO 4674-1 method 2<br />
weft 5,15<br />
elongation up to break after climatic chamber -30°C %<br />
warp<br />
4<br />
ISO 1421<br />
weft 3<br />
breaking strength after climatic chamber -30°C daN/5 cm<br />
warp<br />
150<br />
ISO 1421<br />
weft 140<br />
tear strength after climatic chamber +70°C daN<br />
warp<br />
5,3<br />
ISO 4674-1 method 2<br />
weft 4,8<br />
elongation up to break after climatic chamber +70°C %<br />
warp<br />
3,6<br />
ISO 1421<br />
weft 2,9<br />
breaking strength after climatic chamber +70°C daN/5 cm<br />
warp<br />
120<br />
ISO 1421<br />
weft 120<br />
France NF P92-503 M1<br />
Italy UNI 9177 Class 1<br />
fi re classifi cation<br />
Germany DIN 4102 B1<br />
UK BS 5867 C<br />
USA NFPA 701 FR<br />
roll length<br />
30 m<br />
cleaning<br />
confection<br />
EASY<br />
with soapy water<br />
by heat, high frequency or ultrasonic welding<br />
from 2012:<br />
roll length all<br />
interior sunscreens<br />
changes from<br />
50m > 30m<br />
rolls<br />
These properties are given as indicative and don’t have any contractual value<br />