434 R K Dayal and N Parvathavarth<strong>in</strong>i<br />
Figure 1. High pressure steam pipe<br />
conta<strong>in</strong><strong>in</strong>g blow out w<strong>in</strong>dow fracture<br />
(Antonio 1993).<br />
Figure 2. Close-up view <strong>of</strong> the w<strong>in</strong>dow (Antonio 1993).<br />
Figure 3. Cross-section <strong>of</strong> the boiler show<strong>in</strong>g the damage<br />
due to hydrogen (Weiss 1993).<br />
Figure 4. Close-up view <strong>of</strong> the bulge (Weiss 1993).<br />
Figure 5. <strong>Hydrogen</strong>-<strong>in</strong>duced crack<strong>in</strong>g <strong>in</strong> 9Cr–1Mo steel at HAZ / base metal boundary due to repair<br />
weld<strong>in</strong>g without PWHT (Parvathavarth<strong>in</strong>i 1995).