Millathane® 76 Datasheet - TSE Industries, Inc.

70 DUROMETER 80 DUROMETERNON-BLACK SULFUR CUREFORMULATIONPHYSICAL PROPERTIESMillathane ® 76 100.0 Hardness, Durometer, A 68Zinc stearate 0.5 100% Modulus, psi 570AC Poly 617A 1.0 MPa 3.9Translink 555 55.0 200% Modulus, psi 1680Cumar P-10 5.0 MPa 11.6MBTS 4.0 300% Modulus, psi 2640MBT 2.0 MPa 18.2Thanecure ® ZM 1.0 Tensile Strength, psi 3800Sulfur 1.5 MPa 26.2CURE: 15’ @ 155°C (311°F) Elongation, % 490Tear Die C, pli 355kN/m 62.2BLACK SULFUR CUREFORMULATIONPHYSICAL PROPERTIESMillathane 76 100.0 Hardness, Durometer, A 70Zinc stearate 0.5 100% Modulus, psi 669N-550 black 35.0 MPa 4.6TP-95 5.0 200% Modulus, psi 1438MBTS 4.0 MPa 9.9MBT 2.0 300% Modulus, psi 2354Thanecure ZM 1.0 MPa 16.2Sulfur 1.5 Tensile Strength, psi 3433CURE: 10’ @ 155°C (311°F) MPa 23.7Elongation, % 490Tear Die C, pli 346kN/m 60.6NON-BLACK SULFUR CUREFORMULATIONPHYSICAL PROPERTIESMillathane 76 100.0 Hardness, Durometer, A 80Zinc stearate 0.5 100% Modulus, psi 250Cumar P10 10.0 MPa 1.7Hi-Sil 233 50.0 200% Modulus, psi 436AC Poly 617A 2.0 MPa 3.0MBTS 4.0 300% Modulus, psi 7.38MBT 2.0 MPa 5.1Thanecure ZM 1.0 Tensile Strength, psi 2922Sulfur 1.5 MPa 20.2CURE: 15’ @ 155°C (311°F) Elongation, % 671Tear Die C, pli 294kN/m 51.5BLACK SULFUR CUREFORMULATIONPHYSICAL PROPERTIESMillathane 76 100.0 Hardness, Durometer, A 80Zinc stearate 0.5 100% Modulus, psi 812TP-95 10.0 MPa 5.6N-330 black 51.0 200% Modulus, psi 1731AC Poly 617A 1.5 MPa 11.9MBTS 4.0 300% Modulus, psi 2522MBT 2.0 MPa 17.4Thanecure ZM 1.0 Tensile Strength, psi 3499Sulfur 1.5 MPa 24.1CURE: 15’ @ 155°C (311°F) Elongation, % 495Tear Die C, pli 365kN/m 63.9NON-BLACK PEROXIDE CUREFORMULATIONPHYSICAL PROPERTIESMillathane 76 100.0 Hardness, Durometer, A 70Stearic acid 0.5 100% Modulus, psi 480Hi-Sil 233 30.0 MPa 3.3Sartomer SR-297 3.0 200% Modulus, psi 984Di-Cup 40C 2.0 MPa 6.8CURE: 15’ @ 160°C (320°F) 300% Modulus, psi 2059MPa 14.2Tensile Strength, psi 3560MPa 24.6Elongation, % 386Tear Die C, pli 256kN/m 44.8NON-BLACK PEROXIDE CUREFORMULATIONPHYSICAL PROPERTIESMillathane 76 100.0 Hardness, Durometer, A 80Stearic acid 0.5 100% Modulus, psi 807SR-297 7.5 MPa 5.6Hi-Sil 233 25.0 200% Modulus, psi 1754AC Poly 617A 2.0 MPa 12.1Di-Cup 40C 3.0 300% Modulus, psi ––CURE: 15’ @ 160°C (320°F) MPa ––Tensile Strength, psi 3341MPa 23.0Elongation, % 296Tear Die C, pli 202kN/m 35.4BLACK PEROXIDE CUREFORMULATIONPHYSICAL PROPERTIESMillathane 76 100.0 Hardness, Durometer, A 70Stearic acid 0.5 100% Modulus, psi 462Struktol WB222 0.2 MPa 3.2TP-95 4.0 200% Modulus, psi 1572N-550 black 35.0 MPa 10.8Di-Cup 40C 2.0 300% Modulus, psi 2805CURE: 15’ @ 160°C (320°F) MPa 19.3Tensile Strength, psi 3429MPa 23.6Elongation, % 363Tear Die C, pli 318kN/m 55.7BLACK PEROXIDE CUREFORMULATIONPHYSICAL PROPERTIESMillathane 76 100.0 Hardness, Durometer, A 80Stearic acid 0.5 100% Modulus, psi 986TP-95 10.0 MPa 6.8N-774 70.0 200% Modulus, psi 2349SR 297 7.5 MPa 16.2Di-Cup 40C 3.0 300% Modulus, psi ––CURE: 15’ @ 160°C (320°F) MPa ––Tensile Strength, psi 2642MPa 18.2Elongation, % 251Tear Die C, pli 200kN/m 35.0TSE INDUSTRIES, INC. (800) 237-7634 MILLATHANE 76 7/04 pg. 15