Millathane® 76 Datasheet - TSE Industries, Inc.
Millathane® 76 Datasheet - TSE Industries, Inc.
Millathane® 76 Datasheet - TSE Industries, Inc.
You also want an ePaper? Increase the reach of your titles
YUMPU automatically turns print PDFs into web optimized ePapers that Google loves.
CARBON BLACK, N-220 (ISAF)Press Cured 15’ @ 154°C (309°F)PHYSICAL PROPERTIESParts per 100 polymer 20 40 60Hardness, Durometer A 60 78 88100% Modulus, psi 352 690 1111MPa 2.4 4.8 7.7200% Modulus, psi 740 1600 2252MPa 5.1 11.0 15.5300% Modulus, psi 1311 2534 2941MPa 9.0 17.5 20.3Tensile Strength, psi 4714 4252 3222MPa 32.5 29.3 22.2Elongation, % 620 521 365Tear Strength, pli 368 378 375kN/m 64.4 66.2 65.7Compression Set, % 42.5 44.2 47.922 hrs @ 70°C (158°F)Taber Abrasion mg loss, 6.5 6.5 8.0H-18 wheel, 1000 g loadCARBON BLACK, N-550 (FEF)Press Cured 10’ @ 154°C (309°F)PHYSICAL PROPERTIESParts per 100 polymer 20 40 60Hardness, Durometer A 60 75 85100% Modulus, psi 329 666 1591MPa 2.3 4.6 11.0200% Modulus, psi 723 1438 2595MPa 5.0 9.9 18.0300% Modulus, psi 1272 2354 2982MPa 8.8 16.2 20.6Tensile Strength, psi 4171 3433 3067MPa 28.8 23.7 21.2Elongation, % 564 490 331Tear Strength, pli 342 346 377kN/m 59.9 60.6 66.0Compression Set, % 51.7 43.3 46.722 hrs @ 70°C (158°F)Taber Abrasion mg loss, 7.0 4.0 7.0H-18 wheel, 1000 g loadCARBON BLACK, N-330 (HAF)Press Cured 10’ @ 155°C (311°F)PHYSICAL PROPERTIESParts per 100 polymer 20 40 60Hardness, Durometer A 65 75 88100% Modulus, psi 478 683 10<strong>76</strong>MPa 3.3 4.7 7.4200% Modulus, psi 920 1442 2211MPa 6.3 9.9 15.2300% Modulus, psi 1519 2220 2923MPa 10.5 15.3 20.2Tensile Strength, psi 4009 3886 3280MPa 27.6 26.8 22.1Elongation, % 590 531 390Tear Strength, pli 351 347 329kN/m 61.5 60.8 57.6Compression Set, % 42.3 46.8 43.622 hrs @ 70°C (158°F)Taber Abrasion mg loss, 6.0 5.0 8.0H-18 wheel, 1000 g loadCARBON BLACK, N-774 (SRF)Press Cured 11’ @ 154°C (309°F)PHYSICAL PROPERTIESParts per 100 polymer 20 40 60Hardness, Durometer A 66 68 82100% Modulus, psi 263 337 832MPa 1.8 2.3 5.7200% Modulus, psi 521 723 1690MPa 3.6 5.0 11.7300% Modulus, psi 991 1207 2338MPa 6.3 8.3 16.1Tensile Strength, psi 3473 3116 3118MPa 24.0 21.5 21.5Elongation, % 677 646 481Tear Strength, pli 312 333 362kN/m 54.7 58.3 63.4Compression Set, % 49.9 52.2 54.922 hrs @ 70°C (158°F)Taber Abrasion mg loss, 8.0 7.0 8.0H-18 wheel, 1000 g loadCARBON BLACK, N-326 (HS-HAF)Press Cured 11’ @ 154°C (309°F)PHYSICAL PROPERTIESParts per 100 polymer 20 40 60Hardness, Durometer A 58 74 80100% Modulus, psi 219 598 663MPa 1.5 4.1 4.6200% Modulus, psi 409 11<strong>76</strong> 1328MPa 2.8 8.1 9.2300% Modulus, psi 1072 1823 1933MPa 7.4 12.6 13.3Tensile Strength, psi 4546 3740 2828MPa 31.3 27.8 19.5Elongation, % <strong>76</strong>6 569 523Tear Strength, pli 306 394 342kN/m 53.6 69.0 59.8Compression Set, % 53.8 59.2 62.722 hrs @ 70°C (158°F)Taber Abrasion mg loss, 6.0 8.0 8.0H-18 wheel, 1000 g loadCARBON BLACK, N-990 (MT)Press Cured 11’ @ 154°C (309°F)PHYSICAL PROPERTIESParts per 100 polymer 20 40 60Hardness, Durometer A 52 60 65100% Modulus, psi 191 310 427MPa 1.3 2.1 2.9200% Modulus, psi 341 639 867MPa 2.4 4.4 6.0300% Modulus, psi 596 1145 1446MPa 4.1 7.9 10.0Tensile Strength, psi 3389 3032 2386MPa 23.4 20.9 16.5Elongation, % 710 629 551Tear Strength, pli 257 309 306kN/m 45.0 54.1 53.6Compression Set, % 53.6 53.9 53.822 hrs @ 70°C (158°F)Taber Abrasion mg loss, 7.0 8.0 8.0H-18 wheel, 1000 g load<strong>TSE</strong> INDUSTRIES, INC. (800) 237-<strong>76</strong>34 MILLATHANE <strong>76</strong> 7/04 pg. 17