<strong>MIL</strong>-<strong>PRF</strong>-<strong>13830B</strong><br />
APPENDIX D<br />
D.4.3.2 Normal conditions (room temperature)..Strength properties shall be<br />
determined for room temperature adhesive at 23° ± 2°C, no sooner than 10 minutes<br />
after specimens have reached equilibrium at such temperature.<br />
D.4.3.3 Elevated temperature Conditions. Conditioning of specimens for elevated<br />
temperature shear strength tests shall require a suitable oven to maintain the<br />
specimen at 71° ± 2°C for a period of 60 minutes prior to testing.<br />
D.4.3.4 Low temperature conditions Conditioning of specimens for low<br />
temperature shear strength tests shall require a suitable conditioning chamber to<br />
maintain the specimens at -51° ± 2°C for a period of 60 minutes prior to testing.<br />
D.4.3.5 Humidity conditions. Conditioning of specimens for humidity shear<br />
strength tests shall require a suitable conditioning chamber to maintain the<br />
specimen at 71° ± 2°C and 95 to 100% relative humidity for a period of 10 days prior<br />
to testing.<br />
D.4.4 Preparation of test specimens.<br />
D.4.4.1 Preparation of shear test specimens. Test specimens as shown in<br />
Figure 1D shall be prepared in sufficient quantities for all the necessary tests.<br />
Specimens for testing all the Table 1 properties shall be prepared from 0.32 cm (min)<br />
by 2.54 cm by 10 cm 2024-T3 aluminum conforming to ANSI/SAE AMS 4035; and<br />
glass microslides 2.54 cm by 2.54 cm by 0.30 cm (min). The cleaning, priming, and<br />
bonding procedures shall be in accordance the manufacturer’s instruction sheet.<br />
The test specimens are to be assembled as shown in Figure 1D with the glass forming<br />
a bond of 6.45 sq. cm to one aluminum adherent and 3.23 sq. cm to the other<br />
aluminum adherent.<br />
D 4.4.2 Preparation of thermal and mechanical shock stability test specimens.<br />
Test specimens shall be prepared in sufficient quantities for all the necessary tests.<br />
Specimens for testing the thermal and mechanical properties shall consist of right<br />
angle optical glass prisms 4 cm x 4 cm x 4 cm bonded to an aluminum plate<br />
6 cm x 6 cm x 1.0 cm. The priming and bonding procedures shall be in accordance<br />
with the manufacturer’s instruction sheet.<br />
D.4.5. Qualification tests.<br />
D.4.5.1 Qualification retest. Unless otherwise specified by the qualifying activity,<br />
adhesives which have previously passed the qualification tests but have subsequently<br />
60<br />
Source: http://www.assistdocs.com -- Downloaded: 2006-05-24T15:32Z<br />