Rapport 957.pdf - Pure

VÄRMEFORSKInnehållsförteckning1 INLEDNING .......................................................................................................................... 11.1 BAKGRUND......................................................................................................................... 11.2 PROBLEM ........................................................................................................................... 31.3 SYFTE................................................................................................................................31.4 BEGREPP OCH DEFINITIONER............................................................................................... 42 METODIK ............................................................................................................................. 52.1 PROVTAGNING OCH BEREDNING AV ASKORNA....................................................................... 52.2 MÄTNING AV GASUTVECKLING............................................................................................ 102.3 ANALYS AV KEMISK SAMMANSÄTTNING OCH PH FÖR ASKORNA ............................................ 122.4 SVEPELEKTRONMIKROSKOPI (SEM/EDS) OCH PULVERRÖNTGENDIFFRAKTION (XRD)AV ASKORNA..................................................................................................................... 132.5 ANALYS AV METALLISKT ALUMINIUM I BRÄNSLET.................................................................. 132.6 TERMODYNAMISKA BERÄKNINGAR...................................................................................... 133 RESULTAT......................................................................................................................... 163.1 ASKORNAS GASUTVECKLING.............................................................................................. 163.2 ASKORNAS KEMISKA SAMMANSÄTTNING OCH PH................................................................. 193.3 RESULTAT FRÅN SVEPELEKTRONMIKROSKOPI (SEM/EDS) OCH PULVERRÖNTGEN-DIFFRAKTION (XRD) ......................................................................................................... 223.4 BRÄNSLETS KEMISKA SAMMANSÄTTNING ............................................................................ 263.5 RESULTAT FRÅN TERMODYNAMISKA BERÄKNINGAR ............................................................. 274 RESULTATANALYS.......................................................................................................... 314.1 GASBILDNING (ANALYSMETODEN, EFFEKT AV OXIDATION, BILDADE GASER,REAGERANDE METALLER) .................................................................................................. 314.2 SAMBAND MELLAN ASKANS KEMISKA SAMMANSÄTTNING OCH DESS GASUTVECKLING............. 364.3 SAMBAND MELLAN ASKTYP OCH ASKANS GASBILDNINGSPOTENTIAL SAMTMELLAN PANNTYP OCH ASKANS GASBILDNINGSPOTENTIAL ................................................... 404.4 SAMBAND MELLAN BRÄNSLETS SAMMANSÄTTNING OCH ASKANS GASUTVECKLING ................. 424.5 SAMBAND MELLAN RÖKGASTEMPERATUR OCH FLYGASKANS GASUTVECKLING ...................... 444.6 MÖJLIGA REAKTIONSVÄGAR FÖR ALUMINIUM SAMT TERMODYNAMISKA BERÄKNINGAR........... 454.7 HUR KAN METALLISKT ALUMINIUM ÖVERLEVA FÖRBRÄNNINGEN?.......................................... 495 SLUTSATSER.................................................................................................................... 516 REKOMMENDATIONER.................................................................................................... 527 FÖRSLAG TILL FORTSATT FORSKNINGSARBETE ..................................................... 538 LITTERATURREFERENSER ............................................................................................ 54BILAGORA BESKRIVNING AV ANLÄGGNINGARNABCDEDATA FRÅN TOTALHALTSANALYSER AV ASKORINSAMLADE BRÄNSLEANALYSERDATA FRÅN SEM-ANALYSERGASUTVECKLING HOS ASKOR FRÅN HÖGDALEN, UPPSALA OCH SÖDERENERGI– SLUTRAPPORT 2004-11-23ix