Figure 4.38 shows EDS analysis <strong>of</strong> the sample CR30F. Accord<strong>in</strong>g to EDS<br />
results <strong>of</strong> the sample, the concentration content <strong>of</strong> Al and Cu changes and copper is<br />
diff<strong>use</strong>d <strong>in</strong>to alum<strong>in</strong>a approximately 50µm at 1350 o C.<br />
Wt (%)<br />
70<br />
60<br />
50<br />
40<br />
30<br />
20<br />
10<br />
0<br />
Al (wt%) Cu (wt%)<br />
0 50 100 150 200 250<br />
Distance (µm)<br />
Figure 4.38. EDS l<strong>in</strong>e analysis <strong>of</strong> the sample CR30F.<br />
56