Murray, J. L., 1987, Ed., ASM International. p. 1-5. Nakajima, H., 1997, The discovery and acceptance <strong>of</strong> the Kirkendall effect: the result <strong>of</strong> a short research career, JOM. 49: p. 15-19. Oocities, December 2011, Metallurgy <strong>of</strong> steel, http://www.oocities.org/ferritec_eng/chapter_1.htm Paul, A., 2004, The Kirkendall effect <strong>in</strong> solid state diffusion, E<strong>in</strong>dhoven. Rahaman, M. N., 1995, Ceramic Process<strong>in</strong>g and S<strong>in</strong>ter<strong>in</strong>g, Marcel Dekker. Ramlee, N. B., 2008, Effect <strong>of</strong> pH, temperature and chloride concentration on the corrosion behaviour <strong>of</strong> welded 316L sta<strong>in</strong>less steel, Universiti Technology Malaysia. Sadowski, T. and Samborski, S., 2007, Development <strong>of</strong> damage state <strong>in</strong> porous ceramics under compression. Computational Materials Science. 43(1): p. 75-81. Sepulveda, P. and B<strong>in</strong>ner, J. G. P., 1999, . Process<strong>in</strong>g <strong>of</strong> Cellular Ceramics by Foam<strong>in</strong>g and <strong>in</strong> situ Polymerisation <strong>of</strong> Organic Monomers. Journal <strong>of</strong> the European Ceramic Society. 19(1): p. 2059-2066. Shackel<strong>for</strong>d, J. F. and Doremus, R. H., 2008, Ceramic and glass materials, Spr<strong>in</strong>ger. Siao, C. Y., Lee, H. W. and Lu, H. Y., 2009, Kirkendall porosity <strong>in</strong> barium titanatestrontium titanate diffusion couple, Ceramic International. 35(7): p. 2951-2958. Silva L. C. C. and Mehl, R. F., 1951, Interface and marker movements<strong>in</strong> diffusion <strong>in</strong> solid solutions <strong>of</strong> <strong>metal</strong>s, Trans. AIME. 191: p. 155-173. Silva L. C. C., 1998, A reflection on Mehl R. F. and the Kirkendall effect, JOM. 50: p. 6-7. Smigelkas, A. D. and Kirkendall E. O., 1947, Z<strong>in</strong>c diffusion <strong>in</strong> alpha brass, Trans. AIME. 171: p. 130-134. Soh, E. and Ruys, A. J., 2009, Characterisation <strong>of</strong> foamed porous alum<strong>in</strong>a tissue scaffolds, Journal <strong>of</strong> Biomimetics. 4: p. 21-26. Sumitomo Chemical, Co. Ltd., 2010, Alum<strong>in</strong>a, http://www.sumitomo-chem.co.jp/english/products/<strong>in</strong>dex.html. Tummala, R. R., 1988, Ceramics <strong>in</strong> microelectronic packag<strong>in</strong>g, American Ceramic Society Bullet<strong>in</strong>. 67(4): p. 752-758. 66
Yalamaç, E., 2010, S<strong>in</strong>ter<strong>in</strong>g, Co-S<strong>in</strong>ter<strong>in</strong>g and Microstructure Control <strong>of</strong> Oxide Based Materials: Zirconia, Alum<strong>in</strong>a, Sp<strong>in</strong>el, Alum<strong>in</strong>a-Zirconia and Sp<strong>in</strong>el-Alum<strong>in</strong>a, Izmir Institute <strong>of</strong> Technology. 67
- Page 1 and 2:
USE OF METAL TEMPLATES FOR MICROCAV
- Page 3 and 4:
ACKNOWLEDGEMENTS I would like to ex
- Page 5 and 6:
ÖZET ALÜMİNA İÇİNDE MİKROBO
- Page 7 and 8:
4.3.1. Alumina ....................
- Page 9 and 10:
Figure 3.4. Pressed samples: (a) be
- Page 11 and 12:
Figure 4.35. Phase equilibrium diag
- Page 13 and 14:
CHAPTER 1 INTRODUCTION Porous oxide
- Page 15 and 16:
2.1. Porous Materials CHAPTER 2 LIT
- Page 17 and 18:
Alumina ceramic is one of the most
- Page 19 and 20:
2.3. Properties and Applications of
- Page 21 and 22:
Selection of stainless steels based
- Page 23 and 24:
Some physical properties of copper
- Page 25 and 26:
of some of the oxygen from the air
- Page 27 and 28: not occupied by the flow of Cu from
- Page 29 and 30: During the 4 hours soaking time at
- Page 31 and 32: y the technique of dilatometry (Rah
- Page 33 and 34: CHAPTER 3 EXPERIMENTAL In this chap
- Page 35 and 36: Table 3.1. Properties of alumina po
- Page 37 and 38: 3.2.1. Co-Pressing with Single-acti
- Page 39 and 40: 3.3. Density Measurements The final
- Page 41 and 42: Figures 4.3 and 4.4 show relative d
- Page 43 and 44: Densification Rate (1/ o C) 0,005 0
- Page 45 and 46: Densification Rate (1/ o C) 0,009 0
- Page 47 and 48: (a) (b) (c) (d) (e) Figure 4.8. SEM
- Page 49 and 50: Figure 4.10. EDS analysis of the Ti
- Page 51 and 52: 4.3.3. Ti Diffusion into Alumina In
- Page 53 and 54: Titanium advanced through alumina a
- Page 55 and 56: Wt (%) Wt (%) 100 80 60 40 20 0 100
- Page 57 and 58: Figure 4.22. EDS line analysis of t
- Page 59 and 60: Densification Rate (1/ o C) 0,0069
- Page 61 and 62: Figure 4.27, 28 and 29 belong to ED
- Page 63 and 64: 4.3.5. Stainless Steel Diffusion in
- Page 65 and 66: Wt (%) 50 45 40 35 30 25 20 15 10 5
- Page 67 and 68: Wt (%) 70 60 50 40 30 20 10 0 Al (w
- Page 69 and 70: 4.3.7. Results of Sintering of Alum
- Page 71 and 72: Wt (%) 40 35 30 25 20 15 10 5 0 Al
- Page 73 and 74: CHAPTER 5 CONCLUSIONS Densification
- Page 75 and 76: REFERENCES Alcoa, Inc., 2010, Alumi
- Page 77: Isobe, T., Tomital, T., Kameshima,