dissertation global and local fracture properties of metal matrix ...

Table 9.7. Data on stress for Specimen Al2O3-15-24h.
Mechanism
σ interf max
[MPa]
HRR-theory Mean-Field theory
Composite Particle Matrix
CODi
[µm]
CODvi
[µm]
θ
[°]
r
[µm]
Particle Size
[µm]
σ mean vi
[MPa]
σ eq vi
σ max vi
σ mean vi
σ eq vi
σ max vi
σ mean vi
σ eq vi
[MPa]
[MPa]
[MPa]
[MPa]
[MPa]
[MPa]
[MPa]
σ max vi
[MPa]
1 6x6 18.9 9 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 Fr.
2 1x1 12.8 39 2 3 1145 369 931 1367 751 932 1106 341 931 1272 Dec.
3 2x1 8.8 26 4 4 1186 370 971 1409 754 972 1146 343 971 1314 Dec.
4 10x8 36.2 38 1 4 1079 346 878 1284 702 877 1043 320 879 1198 Fr.
5 15x9 31.1 32 3 9 1127 355 921 1339 721 921 1089 329 921 1250 Fr.
6 11x11 25.3 38 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 Fr.
7 10x5 10 25 2 3 1151 359 943 1367 730 943 1113 333 943 1276 Fr.
8 13x10 21.4 28 1.5 7…9 1112 348 910 1319 706 909 1076 323 910 1233 Fr.
9 5x8 17.6 43 ≈0 2…4 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 Fr.
10 6x24 34 12 ≈0 8 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 Fr.
11 4x2 16.6 16 1.5 5 1117 347 916 1322 704 914 1080 321 916 1237 Dec.
12 12x6 14.7 38 ≈0 0…1 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 Fr.
13 14x7 17.9 42 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 Fr.
14 4x7 19.1 45 2.5 3 1119 376 901 1346 765 902 1079 347 901 1248 Fr.
15 7x8 14.2 10 3.5 4.5 1155 358 947 1369 728 947 1117 332 947 1279 Dec.
16 6x20 64.6 67 ≈0 0…5 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 Fr.
17 8x9 66 72 ≈0 0…5 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 Fr.
18 6x27 79.7 68 ≈0 0…5 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 Fr.
19 5x15 37.9 74 ≈0 0…6 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 Fr.
20 3x7 34.2 74 ≈0 0…5 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 ≈0 Fr.