EN welding technology

Filler wire
MAG stainless steel filler wires
1.4316 DIN 8556: SG X 2 Cr Ni 19 9
XXfor the following base materials:
1.4301, 1.4306, 1.4308, 1.4311, 1.4303, 1.4310, 1.4319, 1.4541,
1.4550, 1.4552
XXJoint and depositing welding of stainless and acid-resistant Cr and
Cr-Ni steels.
XXNot for use in a medium with high sulphur content.
XXFor operating temperatures from -196°C to 350°C.
XXShield gas: Argon S 1 - S 3, mixed gases
D 300 spool 15.0 kg Article no.
0.8 mm 1132008
1.0 mm 1132010
1.2 mm 1132012
D 200 spool 5.0 kg
0.8 mm 1130238
1.0 mm 1130231
1.4551 DIN 8556: SG X 5 Cr Ni Nb 19 9
XXfor the following base materials:
1.4301, 1.4306, 1.4308, 1.4310, 1.4312, 1.4319, 1.4541, 1.4550
XXTIG or MIG/MAG welding of stainless, austenitic steels
XXNot for use in a medium with high sulphur content.
XXFor operating temperatures up to 400°C, scaling resistant up to
+800°C
XXShield gas: Argon, mixed gases, e.g., M11, M23
D 300 spool 15.0 kg Article no.
1.0 mm 1131610
1.2 mm 1131612
Hardfacing shield gas filler wires
MSG material 6-60 no. 1.4718 DIN 8555
XXMaterials and applications:
Deposit welding on machine parts exposed to wear made of
constructional or cast steel. The welding material has good viscous
strength and is wear-resistant. For bulldozer parts, conveyor screws,
roller crushers, percussion hammers, rollers and running surfaces.
XXVickers hardness: 650 - 775 HV
XXRockwell hardness: 56 - 62 HR
XXShield gas: Argon S 1 - S 3, mixed gases
D 300 spool 15.0 kg Article no.
1.0 mm 1130110
1.2 mm 1130112
1.6 mm 1130116
MAG stainless steel filler wires
1.4430 DIN 8556: SG X 2 Cr Ni Mo 19 12
XXfor the following base materials:
1.4401, 1.4404, 1.4408, 1.4429, 1.4435, 1.4436, 1.4541, 1.4550,
1.4552, 1.4571, 1.4573, 1.4580, 1.4581, 1.4583, 1.6901, 1.6902,
1.6903, 1.6905
XXWelding stainless, cryogenic and austenitic steels. For operating
temperatures up to 400°C
XXShield gas: Argon S 1 - S 3, mixed gases
D 300 spool 15.0 kg Article no.
0.8 mm 1130508
1.0 mm 1130510
1.2 mm 1130512
1.4576 DIN 8556: SG X 5 Cr Ni Mo Nb 19 12
XXfor the following base materials:
1.3401,1.4408, 1.4435, 1.4435, 1.4436, 1.4573, 1.4580, 1.4581,
1.4583
XXDifferent types of steels (black&white joints); steels with a high
carbon content, and hard-to-weld steels, e.g., manganese highcarbon
steel,
buffer layers for hardfacing, viscous nickel steels
XXFor operating temperatures from -120°C (viscous) to 300°C
D 300 spool 15.0 kg Article no.
0.8 mm 1130308
1.0 mm 1130310
1.2 mm 1130312
1.4370 DIN 8556: SG X 10 Cr Ni Mn 18 8
XXfor the following base materials:
1.4301, 1.4306, 1.4308, 1.4312, 1.4401, 1.4404, 1.4408, 1.441 0,
1.4435, 1.4436, 1.4541, 1.4550, 1.4571, 1.4573, 1.4580, 1.4583
with H 1 to H 2
XXWelding of stainless and acid-resistant Cr and Cr-Ni-Mn steels. For
stricter requirements in terms of crack safety and viscosity. Work
hardening. Joint welding on different types of steels (black&white
joints). Temperatures up to 850°C.
XXShield gas: Argon S 1 - S 3, mixed gases
D 300 spool 15.0 kg Article no.
0.8 mm 1130408
1.0 mm 1130410
1.2 mm 1130412
!
Other filler wires for deposit welding, dimensions, alloys, spool
types, and larger volumes on request.
1.4842 DIN 8556: SG X 12 Cr Ni 25 20
XXfor the following base materials:
1.4832, 1.4837, 1.4841, 1.4845, 1.4840
XXWelding heat-resistant austenitic steels. The steel can be used in air
up to 1100°C. Scaling resistant up to 1100 °C
XXShield gas: Argon S 1 - S 3, mixed gases
D 300 spool 7.0 kg Article no.
0.8 mm 1130708
1.0 mm 1130710
1.2 mm 1130712
118