UTP HydroCav - UTP Schweissmaterial

Standards :
DIN 8555 : E 10-UM-40-G
UTP 7114
Rutile coated hardfacing stick electrode
resisting wear by impact and abrasion.
Application field
UTP 7114 is suitable for claddings on machine parts subject to a combination of impact and friction wear.
The tough chromium carbide weld deposit is crack resistant and is used for sliding guidance, metal-to-metal
sealing faces, valve seats, conveyor rolls. Buffer layers are generally not necessary. It is used for operating temperatures
up to 200° C.
Welding properties
UTP 7114 has excellent welding properties. The fine droplet spray arc results in smooth notch-free seams
with good slag removal. The weld deposit is still machinable.
Hardness of the pure weld metal
35 HRC
Weld metal analysis in %
C
1,2
Welding instruction
Clean welding area to metallic bright. Pre-heating temperature is linked to the welding application (150 –
400° C). On non- and low-alloyed steels, at least 3 layers should be applied.
Current type DC (+) / AC
Availability / Current adjustment
Stick electrodes
Amperage
Si
1,0
Ø mm x L
A
Cr
18,0
Ni
6,0
Welding positions
2,5 x 350
70 – 100
Fe
balance
PA PB
119