UTP HydroCav - UTP Schweissmaterial

Standards :
EN 1600 : EZ 17 5 1 B 4 2
UTP 6655 Mo
Basic coated stick electrode for17 %
Cr-, 5 % Ni steels
Application field
UTP 6655 Mo is a basic coated stick electrode for joining and surfacing on Cr-steels / cast steels with 16
% Cr, 5 % Ni, 1 % Mo, used in the water turbine - and pump construction
Base materials
1.4405, 1.4418
Properties of the weld metal
The weld deposit of UTP 6655 Mo is stainless as resistant to corrosion as similar 17%-Ni steels. It has a
high resistance to corrosion and vibratory corrosion.
Mechanical properties of the weld metal
Yield strength
R p0,2
MPa
700
Weld metal analysis in %
Tensile strength
R m
MPa
900
Elongation
A
%
15
Impact strength
K v
Joule
40
C Si Mn Cr Ni Mo Fe
0,03 0,3 0,6 17,0 5,0 1,0 balance
Welding instructions
For similar and sissimilar steels up to a 10 mm wall thickness, preheating of 100-150 °C has to be kept. Above
10 mm 150 - 200 °C. Re-drying 2 h at 250-300° C.
Current type
= +
Availability / Current adjustments
Stick electrodes
Amperage
* available on request
Ø mm x L
A
Welding positions
2,5 x 300*
60 – 80
3,2 x 350*
90 - 110
PA PB PC PE PF
4,0 x 400*
110 - 140
321