UTP HydroCav - UTP Schweissmaterial

Standards :
EN ISO 14172 : E Ni 1069
(NiMo28Fe4Cr)
AWS A5.11 : E NiMo-11
UTP 6202 Mo
Basic coated NiMo stick electrode for
highest corrosion requirements
Application field
UTP 6202 Mo is suited for joining materials of the same nature, e. g. alloy B 3 (UNS 10629, NiMo29Cr,
material-No. 2.4600), alloy B 2 (NiMo28, Material-No. 2.4617) or other NiMo-alloys with similar chemical
composition such as for surfacing on low alloyed steels.
UTP 6202 Mo is used in the chemical process industry, especially for processes involving sulphuric-, hydrochloric-
and phosphoric acid.
Properties of the weld metal
Good resistance against hydrogen chloride, sulphuric -, acetic - and phosphoric acids. Intermetallic precipitation
will be largely avoided.
Mechanical properties of the weld metal
Yield strength
R e
MPa
> 450
Weld metal analysis in %
Welding instructions
Grind and clean base material on each side of the weld. Weld with the lowest possible heat input and minimum
interpass temperature. String beads are welded. Quick cooling is advisable to reduce intermetallic
precipitation in the heat affected zone. Re-dry the stick electrodes 2 – 3 hours at 250 – 300° C before use
and weld them out of a warm electrode carrier.
Current type DC (+)
Stick electrodes
Amperage
Ø mm x L
A
Tensile strength
R m
MPa
> 700
2,5 x 300
50 – 70
Elongation
A
%
> 30
3,2 x 300
70 – 90
Impact strength
K v
Joule
> 80
C Si Mn P S Cr Mo Ni Nb Co Al Fe
0,01 0,2 0,5 0,015 0,015 1,0 27,5 balance < 0,5 < 0,5 < 0,5 3,0
Availability / Current adjustment
Welding positions
PA PB PC PE PF
4,0 x 350
90 – 120
29