UTP HydroCav - UTP Schweissmaterial

Standards :
EN ISO 14172 : E Ni 6620 (NiCr14Mo7Fe)
AWS A5.11 : ENiCrMo-6
70
UTP 7013 Mo
High performance stick electrode, welding
in a.c. 120 % recovery
Application field
The high-nickel stick electrode UTP 7013 Mo is especially suited for welding cold-tough nickel steels,
such as X8Ni9.
Welding properties
UTP 7013 Mo is destinated for welding with ac. It is weldable in all positions. Stable arc, easy slag
removal.
Mechanical properties of the weld metal
Weld metal analysis in %
C
0,05
Yield strength
R p0,2
MPa
> 420
Welding instructions
The weld zone must be clean and properly degreased. Prior to welding, the stick electrodes must be dried
for 2 –3 hours at 250 –300° C. The stick electrode is welded with a slight tilt, short arc and sufficiently high
amperage adjustment. To avoid end crater cracks, the crater must be filled properly and the arc drawn away
to the side.
Current type DC (+) / AC
Availability / Current adjustment
Stick electrodes
Amperage
Approval
BV
Si
< 0,6
Ø mm x L
A
Mn
3,5
Tensile strength
R m
MPa
> 690
Cr
13,0
2,5 x 300
50 – 70
Mo
7,0
Welding positions
3,2 x 300
80 – 120
Elongation
A
%
> 35
Ni
balance
Nb
1,6
Impact strength
K v
Joule
> 70 (at –196° C)
W
1,6
Fe
7,0
PA PB PC PE PF
4,0 x 350
110 – 150
5,0 x 400
120 – 160