EFFECTS OF EXTRUSION BLOW MOLDING INTERNAL COOLING ...

More documents

Recommendations

Info

Figure 12. Container Rotation Callouts Parting Line 2.2.4 Compression Testing Objective: Column crush tests provide information about the crushing properties of blown thermoplastic containers. Column crush properties include the crushing yield load, deflection at crushing yield load, crushing load at failure, and apparent crushing stiffness. Equipment: Lansmont Corporation Squeezer Compression Tester (0.1 lbs, 0.001 in) Mettler AE 160 Scale (0.0001g) Methods: Crush testing was performed in accordance with ASTM D 2659-95 Standard Test Method for Column Crush Properties of Blown Thermoplastic Containers (ASTM 28
D 2659, 1995). Twenty samples from each manufacturing method were tested as shown in Figure 13 to determine crushing yield load, deflection at crushing yield load, crushing load at failure, and apparent crushing stiffness. A modified closure was applied to the container. The closure had a vent hole which allowed air to escape during testing as shown in Figure 14. The crown of the closure prevented the hole from sealing and causing pressure to build in the container which could affect compression strength. Figure 13. Compression Testing Setup PLATEN AXIS <strong>OF</strong> CRUSHING PLATEN 29
Page 1 and 2: EFFECTS OF EXTRUSION BLOW MOLDING I
Page 3 and 4: Copyright by Kirk Alan Valko 2004
Page 5 and 6: TABLE OF CONTENTS LIST OF TABLES ..
Page 7 and 8: LIST OF TABLES Table 1. Fasti Cost
Page 9 and 10: Figure 24. Assembly Drawing........
Page 11 and 12: 1 - INTRODUCTION AND LITERATURE REV
Page 13 and 14: The process of extrusion blow moldi
Page 15 and 16: and dropped onto the conveyor, the
Page 17 and 18: Internal cooling is the process of
Page 19 and 20: pin is entering the bottle finish.
Page 21 and 22: 1.3.3 Costs Total cost of the unit
Page 23 and 24: Figure 7. Machine Surround Before F
Page 25 and 26: Table 2. Effect of Decreased Crysta
Page 27 and 28: 1.4.2 Wall thickness In addition to
Page 29 and 30: 2 - EXPERIMENTAL DESIGN AND TEST ME
Page 31 and 32: to determine the connection between
Page 33 and 34: 2.2 Experimental Methods 2.2.1 Samp
Page 35 and 36: Average temperature, checked by the
Page 37: Table 5. Bottle Body Dimension Tole
Page 41 and 42: Figure 15. Compression Data Example
Page 43 and 44: Figure 16. DSC Sample Pan Crimper T
Page 45 and 46: 3 - DATA AND RESULTS 3.1 Cycle time
Page 47 and 48: Table 7. Dimensional Test Result Co
Page 49 and 50: 3.3 Compression Strength Compressio
Page 51 and 52: Table 10. Percent Crystallinity of
Page 53 and 54: Table 12. Percent Crystallinity at
Page 55 and 56: wall thickness. Compression strengt
Page 57 and 58: performance tests. It would be desi
Page 59 and 60: 5.8 Optical Microscopy Optical micr
Page 61 and 62: 51 APPENDIX A Dimensional Results T
Page 63 and 64: 53 Table 15. Dimensional Test Resul
Page 65 and 66: Figure 18. Conventional Wall Thickn
Page 67 and 68: Figure 22. Fasti Wall Thickness 2 0
Page 69 and 70: Table 18. Compression Test Results
Page 71 and 72: Bekum Blow Molder Operating Instruc
Page 73 and 74: a) “SP1”(set point one) tempera
Page 75 and 76: i) Only one function may be used at
Page 77 and 78: ) Use Screwdriver to turn catch abo
Page 79 and 80: Figure 25. Detail 01 - Adaptor 69
Page 81 and 82: Figure 27. Detail 03 - Cooling Slee
Page 83 and 84: Figure 29. Detail 05 - Tip 73
Page 85 and 86: APPENDIX E Fasti Setup Experiment E
Page 87 and 88: Data Analysis Figures 31, 32, and 3
Page 89 and 90:
Figure 31. Main Effects Plot for Fa
Page 91 and 92:
BIBLIOGRAPHY ASTM Standard D2463-95
show all

EFFECTS OF EXTRUSION BLOW MOLDING INTERNAL COOLING ...

Create successful ePaper yourself

Delete template?

Save as template?