immersion was poor although the coating supplier claims that no additional paint system<br />
is necessary.<br />
H.3.3<br />
Tensile tests on tapered specimens<br />
Paint adhesion was determined by low-temperature (-50 o C) testing of coated and painted<br />
specimens. As compared to the Sermetel adhesion, the paint adhesion on the metallic<br />
coatings was poor. Complete paint delamination occurred for deformations larger than<br />
3%.<br />
H.4 Conclusions<br />
The cross-cut tests show that good paint adhesion may be achieved with metal coatings.<br />
An important factor is the time delay between passivation and the application of a primer.<br />
Data obtained by NLR indicate that if the passivated surfaces are exposed to the<br />
atmosphere for too long, poor paint adhesion may be obtained.<br />
H.5 References<br />
[H1]<br />
t’Hart W.G.J. and Boogers J.A.M., Coatings considered for cadmium<br />
substitution Garteur AG17 Programme, NLR-CR-97107 L<br />
[H2] Marchandise, D., Synthesis of Aerospatiale Results, (1996)<br />
Page 94<br />
GARTEUR SM/AG17 TP128