31. Devillers, M., Sirch, M., and Penzhorn, R.-D., Journal of Nuclear Materials, 1993. 207: p. 53-61. 32. Simonovic, B.R., Mentus, S, Dimitrijevic, R., and Susic, M.V., International Journal of Hydrogen Energy, 1999. 24: p. 449-454. 33. Libowitz, G.G., Hayes, H.F., and Gibb, T.R.P., Journal of Physical Chemistry, 1958. 62: p. 76-79. 34. Brundle, C.R., Physical Review Letters, 1978. 40: p. 972-975. 35. Giza, K., Iwasieczko, W., Drulis, H., Pavlyuk, V.V., and Bala, H., Materials Science and Engineering, 2001. A303: p. 158-162. 36. Chen, J., Dou, S.X., and Liu, H.K., Journal of Power Sources, 1996. 63: p. 267- 270. 37. Bowman, R.C., Luo, C.H., Ahn, C.C., Witham, C.K., and Fultz, B., Journal of Alloys and Compounds, 1995. 217: p. 185-192. 38. Witham, C., Jr, R.C. Bowman, and Fultz, B., Journal of Alloys and Compounds, 1997. 254: p. 574-578. 39. Rozdzynska-Kielbik, B., Iwasieczko, W., Drulis, H., Pavlyuk, V.V., and Bala, H., Journal of Alloys and Compounds, 2000. 298: p. 237-243. 40. Mendelsohn, M. H., Gruen, D. M., and Dwight, A.E., Nature, 1977. 269: p. 45- 47. 41. Nishimura, K., Sato, K., Nakamura, Y., Inazumi, C., Oguro, K., Uehara, I., Fujitani, S., and Yonezu, I., Journal of Alloys and Compounds, 1998. 268: p. 207- 210. 42. Luo, S., Luo, W., Clewley, J.D., Flanagan, T.B., and Wade, L.A., Journal of Alloys and Compounds, 1995. 231: p. 467-472. 43. Flanagan, T.B. and Oates, W.A., Thermodynamics of Intermetallic Compound- Hydrogen Systems, in Hydrogen in Intermetallic Compounds I, Schlapbach, L., Editor. 1988, Springer-Verlag: Heidelberg. 44. Cohen, R.L. and West, K.W., Journal of Less Common Metals, 1983. 95: p. 17- 23. 45. Uchida, H., International Journal of Hydrogen Energy, 1999. 24: p. 861-869. 46. Goodell, P.D., Journal of Less Common Metals, 1984. 99: p. 1-14. 86
47. Suryanarayana, C., Progress in Materials Science, 2001. 46: p. 1-184. 48. Msika, E., Latroche, M., Cuevas, F., and Percheron-Guegan, A., Materials Science and Engineering B, 2004. 108(1-2): p. 91-95. 49. Aoyagi, H., Aoki, K., and Masumoto, T., Journal of Alloys and Compounds, 1995. 231: p. 804-809. 50. Petrucci, R.H., Harwood, W.S., and Herring, G., General Chemistry: Principles and Modern Applications, 8th ed. 2001: Prentice-Hall. 51. http://cst-www.nrl.navy.mil/lattice/spcgrp/hexagonal.html. 52. Peisl, H., Lattice Strains Due to Hydrogen in Metals, in Hydrogen in Metals I, G. Alefeld, J.V., Editor. 1978, Springer-Verlag: Heidelberg. p. 53-74. 53. Seta, S. and Uchida, H., Journal of Alloys and Compounds, 1995. 231: p. 448- 453. 54. Yvon, K. and Fischer, P., Crystal and Magnetic Structures of Ternary Metal Hydrides: A Comprehensive Review, in Hydrogen in Intermetallic Compounds I, Schlapbach, L., Editor. 1992, Springer-Verlag: Heidelberg. p. 87-138. 55. Andersen, A.F., in Hydrides for Energy Storage, A.F. Andersen, A.J.M., Editor. 1978, Pergamon: U.K. p. 61-72. 56. Furrer, A., Fischer, P., Halg, W., and Schlapbach, L., in Hydrides for Energy Storage, A.F. Andersen, A.J.M., Editor. 1978, Pergamon Press: U.K. p. 73-82. 57. Smith, W.F., Foundations of Materials Science and Engineering. 2004, New York: Mc Graw Hill. 58. Hashimoto, Y., Asano, K., and Iijima, Y., Materials Transactions, 2002. 43(11): p. 2696-2702. 59. Jurczyk, M., Smardz, K., Rajewski, W., and Smardz, L., Materials Science and Engineering, 2001. A303: p. 70-76. 60. Smardz, L., Smardz, K., Jurczyk, M., and Jakubowicz, J., Materials Science and Engineering, 2000. 313: p. 192-200. 61. M. J. Rosso, P. M. Golben, Journal of the Less Common Metals, 1987. 131(1-2): p. 283-292. 62. Corre, S., Bououdina, M., Kuriyama, N., Fruchart, D., and Adachi, G., Journal of Alloys and Compounds, 1999. 292: p. 166-173. 87
- Page 1 and 2:
RECOVERY OF HYDROGEN AND HELIUM FRO
- Page 3 and 4:
ABSTRACT Waste streams of hydrogen
- Page 5 and 6:
I dedicate this work to my family m
- Page 7 and 8:
I also would like to cheer for my f
- Page 9 and 10:
2.2.2.1. Hydriding and Dehydriding
- Page 11 and 12:
LIST OF FIGURES Figure 1. Pressure-
- Page 13 and 14:
Figure 34. Pressure profiles under
- Page 15 and 16:
1. INTRODUCTION The focus of this s
- Page 17 and 18:
ecause of the difference in partial
- Page 19 and 20:
hydrides by dissolving large amount
- Page 21 and 22:
hydrogen storage alloy has a specif
- Page 23 and 24:
• Insensitivity to poisoning by i
- Page 25 and 26:
hydrogen capacity was not reproduci
- Page 27 and 28:
showed the lowest plateau pressure
- Page 29 and 30:
grain boundaries increases the tota
- Page 31 and 32:
These parameters are generally inte
- Page 33 and 34:
Figure 4. CaCu5-type P6/mmm structu
- Page 35 and 36:
In this study, the addition of Al t
- Page 37 and 38:
2. EXPERIMENTAL 2.1.Chemicals and R
- Page 39 and 40:
Figure 5. The high energy Spex 8000
- Page 41 and 42:
2.2.1.1. Hydriding and Dehydriding
- Page 43 and 44:
approximately 5 atm, and heating th
- Page 45 and 46:
determined by the start and end of
- Page 47 and 48:
450 400 coating thickness (Å) 350
- Page 49 and 50: 3. RESULTS AND DISCUSSIONS 3.1. Hyd
- Page 51 and 52: DSC 111 heat flow/mW Exo 300 Figure
- Page 53 and 54: The thermogram associated with the
- Page 55 and 56: total time was broken into three 30
- Page 57 and 58: The VTiNi sample was subjected to d
- Page 59 and 60: solid solution of hydrogen rather t
- Page 61 and 62: DSC 111 Heat Flow/mW 180 Exo Figure
- Page 63 and 64: 100 rpm setting, the milling vial w
- Page 65 and 66: BPR, 400 rpm, 5 minutes) did not re
- Page 67 and 68: Table 1: Effects of various milling
- Page 69 and 70: Due to the fast kinetics observed a
- Page 71 and 72: The mole % Al after milling was les
- Page 73 and 74: Figure 24: Percent hydrogen capacit
- Page 75 and 76: the start of the heating period, wh
- Page 77 and 78: However, it was noted that the part
- Page 79 and 80: percent hydrogen was decreased. The
- Page 81 and 82: 3.2.2.4. AuPd and Pt Coating on LaN
- Page 83 and 84: 1.0 0.8 (a) (b) Wt. % H absorbed 0.
- Page 85 and 86: After dehydriding by the sample, th
- Page 87 and 88: 19 18 P (atm) 17 16 15 14 0.74 %Al
- Page 89 and 90: GC output, arbitrary units 0 5 10 1
- Page 91 and 92: sample was LaNi 5 . This may indica
- Page 93 and 94: 30 min. 15 min. Intensity (arb. uni
- Page 95 and 96: After milling the percentages of Al
- Page 97 and 98: 4. CONCLUSIONS This study has been
- Page 99: 16. Van-Vucht, J.H.N., Kuijpers, F.