FILARC flux - Esab

FILARC flux- andmetal- coredwelding wiresFILARC PZ6154PZ6354DIN8555 : MF6-55GPContents page 4DESCRIPTIONWELD METAL COMPOSITIONPrevious pageNext pageThe PZ 6154 (metal-cored) andPZ 6354 (rutile, self-shielding) yield adeposit with a structure consisting ofevenly divided, hard chromium carbidesin a martensitic matrix, having ahardness of Hv 600-700.Very suitable for hardfacing partssubjected to extremely severe conditionsinvolving a combination of impactand abrasion. The weld depositcan only be machined by grinding.The number of layers should be limitedto a maximum of three.Badly worn surfaces are first built-upwith a tougher weld metal, such asthe PZ 6152 or PZ 6153.Applied for hardfacing mill hammers,parts of agricultural equipment, earthmovingequipment and grinders foranimal carcasses.C : 0.50-0.80%Si : 0.60-1.00%Mn: 0.60-1.00%Cr : 4.50-6.50%Mo: 0.80-1.20%SHIELDING GASPZ 6154: CO 2 and Ar/20%CO 2EN 439: C1, M21PZ 6354: none (self-shielded)POSITIONSDEPOSITION DATA IN: CO 2 and Ar/20%CO 2Ø 1.6DiameterStickout1.6mm20mmI V wire Dep. rate[A] [m/min] [kg/h]150 2.4 1.8250 4.5 3.4350 8.4 6.3450 11.9 9.0Diameter2.4mmStickout25mmI V wire Dep. rate[A] [m/min] [kg/h]250 2.5 3.7350 4.3 6.0450 6.8 9.0550 9.0 11.4HARDNESSHardness of 3 rd layer:Hv : 600-700HRC: 55-60CURRENTANDPOLARITYDC +106