FILARC flux- andmetal- coredwelding wiresFFILARC PZ6138AWS A5.29-80 : E81T1-Ni1EN 758-97 : T 46 5 1Ni P M 1 H5Contents page 4Welding parametersPrevious pageNext pageDESCRIPTIONAll-position rutile cored wire for applicationsinvolving thick steel and subzerotoughness. Used in Ar/CO 2 gas.Well established in offshore fabrication.Alloyed with 0.9%Ni combined withTiB micro-alloying, it yields dependableCVN toughness down to -60°C.CTOD tested at -15°C (AW).Weld metal hydrogen falls withinEN758 class H5 for the full parameterenvelope, providing extra security andopportunities to reduce preheating.It has a soft, spatter-free spray arc atall currents and in any welding position,enabling welders to obtain highquality results. Slag releases easily,leaving welds with a smooth tie-inand a nice appearance.In addition, PZ 6138 gives a productivityin PF position several timeshigher than stick electrodes.WELD METAL COMPOSITIONC : 0.04-0.09% P : ≤0.015%Si : 0.30-0.50% S : ≤0.015%Mn: 1.10-1.50%Ni : 0.80-1.10%SHIELDING GASAr/15-25%CO 2EN 439: M21WELD METAL HYDROGENEuronorm 758-95: class H5Typical value in Ar/20%CO 2: 3.6ml/100gFor information on the influence of parameterson the hydrogen level, see page 22-25APPROVALSsee pages13 to17for gradesABSBVContr.DBDNVFORCEGLLRMRSPRSRINATÜVUDTPOSITIONSDEPOSITION DATA IN: Ar/CO 2DiameterStickout1.2mm20mmI V wire Dep. rate[A] [m/min] [kg/h]150 5.6 2.1250 11.1 4.2350 19.8 7.5ALL WELD METAL MECHANICAL PROPERTIESDiameter1.4mmStickout20mmI V wire Dep. rate[A] [m/min] [kg/h]150 3.2 1.8250 6.3 3.6350 11.1 6.3Diameter1.6mmStickout20mmI V wire Dep. rate[A] [m/min] [kg/h]150 2.6 1.8250 4.8 3.3350 7.9 5.4450 11.9 8.1CURRENTANDPOLARITYDC +Tensile strength, R m [MPa]: 550-650Proof stress, R p0.2[MPa]: ≥500Elongation, A 5 [%] : ≥22Impact value, A v (ISO-V) – 20°C [J] : ≥90–40°C [J] : ≥60–60°C [J] : ≥35CERAMICBACKING59