FILARC flux - Esab

FILARC flux- andmetal- coredwelding wiresFILARC PZ6140AWS A5.29-80 : E81T5-Ni2 ~EN 758-97 : T 42 6 2Ni B C 1 H5T 42 6 2Ni B M 1 H5Contents page 4DESCRIPTIONWELD METAL COMPOSITIONPrevious pageNext pageBasic cored wire alloyed with 2.0-2.5%Ni for good CVN toughnessdown to -60°C, both AW and SR.CTOD tested. Ar/CO 2 and CO 2 gas.Providing a very fine short arc droplettransfer, the Ø1.2mm is intended forall-positional welding, including single-sidedroot runs without backing.Above a current level of 200A, Ø1.2requires Ar/CO 2 to obtain spray arc.Ø 1.6mm has a high fill ratio for theproductive welding of single and multi-layerbutt and fillet welds in thepositions PA, PB and PC.Both Ø sizes are also suited for weldingsingle-sided root runs on ceramicbacking strips.PZ 6140 is a productive wire for applicationsinvolving high mechanical properties,thick plates, and high restraint.C : 0.04-0.08% P : ≤0.025%Si : 0.20-0.40% S : ≤0.025%Mn: 0.50-0.90%Ni : 2.00-2.50%SHIELDING GASCO 2 and Ar/15-25%CO 2EN 439: C1, M21WELD METAL HYDROGENEuronorm 758-95: class H5Typical values in Ar/20%CO 2: 1.7ml/100gin CO 2: 1.5ml/100gPOSITIONSDEPOSITION DATA IN: Ar/CO 2DiameterStickout1.2mm20mmI V wire Dep. rate[A] [m/min] [kg/h]150 4.8 2.1250 10.9 4.8350 20.5 9.0ALL WELD METAL MECHANICAL PROPERTIESDiameter1.6mmStickout20mmI V wire Dep. rate[A] [m/min] [kg/h]150 3.1 2.1250 6.3 4.2350 11.7 7.8450 18.9 12.6Tensile strength, R m [MPa]: 500-620Proof stress, R p0.2[MPa]: ≥420Elongation, A 5 [%] : ≥24Impact value, A v (ISO-V) – 40°C [J] : ≥80– 60°C [J] : ≥47CURRENTANDPOLARITYDC –CERAMICBACKING60