FILARC flux - Esab

FILARC flux- andmetal- coredwelding wiresFILARC PZ6129NiAWS A5.20-95 : E71T-5J H4 ~E71T-5MJ H4 ~EN 758-97 : T 42 6 Z B C 1 H5T 42 6 Z B M 1 H5Contents page 4Previous pageNext pageDESCRIPTIONAll-position basic wire for thinnerplates (5-20mm). Alloyed with 0.8%Nifor CVN toughness down to -50°C.Provides a very fine droplet transfer inthe short-arc mode, both in CO 2 andAr/CO 2 gas. Even Ø1.6mm is excellentfor welding single-sided root runs withoutbacking in any position (100A), andfor positional filling and capping (160A).For positions PA, PB and PC at currentsover 200A, Ar/CO 2 is used toobtain spray arc. Single-sided rootruns are now best deposited on ceramicbacking for optimal productivity.It is an excellent wire for high qualitygeneral construction, and for pipewelding in the fixed position with wallthickness >6mm (pipe Ø >150mm).For positional welding of plates > 20mmthickness PZ 6125 is recommended.WELD METAL COMPOSITIONC : 0.05-0.09% P : ≤0.025%Si : 0.40-0.60% S : ≤0.025%Mn: 1.15-1.55%Ni : 0.60-0.90%SHIELDING GASCO 2 and Ar/15-25%CO 2EN 439: C1, M21WELD METAL HYDROGENEuronorm 758-95: class H5Typical values in Ar/20%CO 2: 1.7ml/100gin CO 2: 1.5ml/100g(values valid for 200A welding current)APPROVALSsee pages13 to17for gradesABSBVContr.DNVFORCEGLLRMRSPRSTÜVUDTPOSITIONSDEPOSITION DATA IN: Ar/CO 2DiameterStickout1.2mm20mmI V wire Dep. rate[A] [m/min] [kg/h]150 4.7 2.1250 10.8 4.8350 20.3 9.0ALL WELD METAL MECHANICAL PROPERTIESDiameter1.6mmStickout20mmI V wire Dep. rate[A] [m/min] [kg/h]150 2.8 2.1250 5.2 3.9350 8.8 6.6450 12.8 9.6CURRENTANDPOLARITYDC –Tensile strength, R m [MPa]: 510-600Yield strength, R e[MPa]: ≥420Elongation, A 5 [%] : ≥26Impact value, A v (ISO-V) – 20°C [J] : ≥100– 40°C [J] : ≥60– 60°C [J] : ≥47CERAMICBACKING58