Delivery Program 12-2021

High Strength Thermosetting Resin ▪ HP-E29L / -E56L / -E111L
The Epoxy-Systems HP-E29L, HP-E56L and HP-E111L are unfilled, low viscous 2-component combinations of
resin and hardeners with various processing times between 25 - 110 minutes. Compared to standard resins our
high performance resins show faster curing processes.
The laminates have distinctive static and dynamic strengths and a higher temperature resistance.
Characteristics:
• Very good wetting properties of the reinforcing fibres
• Cold setting, demouldable at room temperature
• Free of solvents and fillers
• Improved physiological compatibility (no R62 labelling)
• Practically shrink-free curing
• Temperature resistance (Tg Max) up to 93°C (HP-E29L)
• Special formulation supports faster curing and increased strength, especially at higher temperatures
• Individual colouring is available upon request
• Excellent adhesion to the In-Mould Coating of HP-Textiles
• In total better characteristic values of approx. 10% (Tg MAX, tensile strength etc.) than those of standard
systems!
Product Properties: Resin Hardener Method
HP-E29L HP-E56L HP-E111L
Colouring colourless light blue-green
Mixing ratio
weight 100 40
Mixed viscosity minutes low viscous
Pot life (at 20°C) minutes
Demouldable after (at 20°C) hours (h)
Demouldable after (at 40°C) hours (h)
Processing temperature optimum °C
Processing temperature minimum °C
25 55 110
24 30 48
6 7 9
15 - 25 20 - 25 20 - 30
15 18 20
Epoxy Resin Systems
Technical
Data Sheet