Delivery Program 12-2021

Infusion-Resin / Laminating Resin
15 min
Article: HP-HTE15GL HARDENER
Processing time approx. 15min. (at 20°C)
Article: HP-HE3000GL
RESIN
200 min
Article: HP-HTE200GL HARDENER
Processing time approx. 200min. (at 20°C)
300 min
Article: HP-HTE300RGL HARDENER
Processing time approx. 300min. (at 20°C)
The basis of the series HP-E3000GL is an unfilled Epoxy-Resin, which is mixable with different hardeners for
every individual purpose. A special feature of this series is a high initial glass transition temperature (Tg) by hardening
at room temperature.
The use of the hardener HP-E200GL increases the maximum glass transition temperature (Tg MAX) up to 107°C.
The series also has a high transparency, so that it is very suitable for visible carbon parts.
Characteristics:
• Extremely low viscosity, so it has a very good fibre wet-out
• High static and dynamic strength
• Pot life time can be freely adjusted between 15 min hardener (HP-E15GL) and 300 min (hardener HP-
E300GL)
• Glass transition temperature (Tg max) up to 107 °C (hardener HP-E200GL)
Epoxy Resin Systems
Product Properties: Resin Hardener Method
HE3000GL HTE15GL HTE200GL HTE300GL
Colour colourless yellowish colourless, clear
Colour
gardner < 1 < 5 < 1 < 1
Mixing ratio
weight 100 30 30 30
Pot life (at 20°C) minutes
15 200 300
Processing temperature optimum °C
20 - 25 20 - 30 20 - 30
Data of unfilled samples. Curing schedule with hardener :
HP-E30RI h at °C 5h/60°C and 6h/80°C
HP-E300RI h at °C 5h/60°C and 6h/80°C
HP-E120RI h at °C 5h/60°C and 6h/80°C (and for Tg max. 2h/120°C)
Technical
Data Sheet
Online Shop
64
phone: +49 (0) 5905-9459870 www.hp-textiles.com mail: info@hp-textiles.com