Mold and Casting Resins<br />
EP-Adhesive-/ Laminate System ▪ HP-E25KL / -45KL<br />
The Epoxy Laminating Resin Systems HP-E25KL and HP-E45KL are unfilled, medium-viscous, chemical resistant<br />
combination of resin and hardener with short or medium processing time (pot life).<br />
They can be used as general-purpose systems for many applications:<br />
as Laminating Resin:<br />
as Mould Resin:<br />
• Excellent wet-out of fibreglass, carbon and<br />
aramid fibres<br />
• Cold-hardening, medium-viscosity,<br />
HP-E25KL: used from 5°C<br />
• Usable as mould making resin<br />
(mixable with colour pigments)<br />
• For coupling-layers (with fillers)<br />
as Covering Layer Resin:<br />
• Clear, tack-free surface<br />
• Usable for repairs / refit of osmosis damages<br />
• High resistance to many chemicals<br />
such as styrene, fuels, ...<br />
• Therefore, they can be used for coatings in tanks,<br />
pipelines, ponds and terrariums<br />
as Adhesive Resin or basic for Fillers:<br />
• Due to a good adhesion for bonding / fillers<br />
can be added<br />
(e. g. combination of HP-PK22 and HP-BF1)<br />
The special formulation allows the usage under difficult conditions (low temperatures, air humidity).<br />
HP-E25KL / HP-E45KL are also free of nonylphenol and contain no reactive diluents!<br />
Please note:<br />
HP-E25KL and HP-E45KL come with a similar resin.<br />
Both hardeners can be mixed among themselves.<br />
Product Properties: Resin Hardener<br />
HP-E25KL HP-E45KL<br />
Colouring colourless light blue-green<br />
Mixing ratio<br />
weight 100 60<br />
Mixed viscosity (at 20°C) mPa s 2500 - 3500 (medium viscous)<br />
Mixed viscosity (at 25°C) mPa s 1400 - 1800 (medium viscous)<br />
Pot life (at 20°C) minutes<br />
25 45<br />
Demouldable after<br />
h<br />