WELDING CONSUMABLE
Iron Powder Electrodes
ESR 14 7014 GENERAL PURPOSE RUTILE ELECTRODE FOR SHEET STEELS
• Heavy Abrasion Moderate Impact
• Non Machinable, Grind Only
• Chrome, Niobium Carbide Matrix
• Easy Strike and Restrike
• Relief Checks in Final Deposit
• Metal Recovery 180%
Preferably used in mild steel fabrication, sheet metal and ornamental iron works on poor fitup joints. Due to it’s iron ­
powder addition in covering, particularly suited for the welding of horizontal fillets grooves with higher speed. Suitable
for all position welding except vertical-down. High current carrying capacity, low spatter. Quite, stable arc characteristics
with fine and fast droplet metal transfer. Very easy arc striking and re-striking. Very smooth welds blending into base
metal without undercuts. Slag is completely self-releasing. Possible to use equally well both with AC and DC.
Hardness
63HRc (1st pass) 62HRc (2nd pass) 64HRc (3rd pass)­ ­
ESR 14 7014 General Purpose Electrode
Part-No Description Pkt Weight
ESR-14-2.5MM-5KG MAGMAWELD 2.5mm 5KG
ESR-14-3.2MM-5KG MAGMAWELD 3.2mm 5KG
ESR-14-4.0MM-6.5KG MAGMAWELD 4.0mm 6.5KG
ESR-14-5.0MM-6.5KG MAGMAWELD 5.0mm 6.5KG
Typical Weldmetal Analysis
C 7.0% Cr 24% Nb 7.0% Fe Balance
DC±
AC
ESH180R E7024 IRON POWDER ELECTRODE
• High Deposition
• Easy Strike and Restrike
• Smooth Stable Arc
• Minimal Spatter
• High Weld Deposition
• Self Releasing Slag
• International Approvals
Classification
AWS/ASME SFA 5.1 E7024 • EN499 E 38 A RR 73 • DIN 1913 E 51 11 RR 11 180
A heavy coated, rutile type high-efficiency electrode having a weld metal recovery of approximately 180 %. It is suited
to producing long fillet welds and economically filling-up large weld sections. The core wire diameters, deviating from ­
standard diameter, are so calculated as to produce definite throat thickness (a=3 to 6 mm). Relatively low current ­
intensities and short burn-off times. ESH180R exhibits good welding properties.
Typical Mechanical Properties of Weld metal
Yield Stress Tensile Strength Elongation Impact Energy ISO - V (J)
>380N/mm² 510-610N/mm² >24% 50@+20°C
Typical Weldmetal Analysis
C: 0.10% Si: 0.40% Mn: 0.90%
ESH180R E7024 IRON POWDER ELECTRODE
Part-No Description Pkt Weight
ESH180R-2.5MM-5KG MAGMAWELD 2.5mm 5KG
ESH180R-3.2MM-6.5KG MAGMAWELD 3.2mm 6.5KG
ESH180R-4.0MM-6.5KG MAGMAWELD 4.0mm 6.5KG
DC-
AC